Filtern
Dokumenttyp
- Vortrag (12)
- Beitrag zu einem Tagungsband (2)
- Zeitschriftenartikel (1)
- Sonstiges (1)
- Posterpräsentation (1)
Schlagworte
- Oberflächenintegrität (9)
- Ultraschallunterstütztes Fräsen (9)
- Werkzeugverschleiß (8)
- Zerspankräfte (5)
- Hochentropielegierung (3)
- Mediumentropielegierung (3)
- WIG-Schweißen (3)
- Surface integrity (2)
- Ultrasonic assisted milling (2)
- Cracking (1)
- Creep-resistant steel (1)
- Digitale Bildkorrelation (DIC) (1)
- Heating rate (1)
- High entropy alloy (1)
- Hochentropiewerkstoff (1)
- Mechanische Eigenschaften (1)
- Medium entropy alloy (1)
- Microstructure characterization (1)
- Rührreibschweißen (1)
- Schweißen (1)
- Stress relief cracking (1)
- Submerged arc welding (1)
- Surface preparation (1)
- TIG welding (1)
- Tool wear (1)
- Verschleißschutz (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (12)
Influence of Surface Preparation on Cracking Phenomena in TIG-Welded High and Medium Entropy Alloys
(2022)
Multi-element systems with defined entropy (HEA—high entropy alloy or MEA—medium entropy alloy) are rather new material concepts that are becoming increasingly important in materials research and development. Some HEA systems show significantly improved properties or combinations of properties, e.g., the overcoming of the trade-off between high strength and ductility. Thus, the synthesis, the resulting microstructures, and properties of HEA have been primarily investigated so far. In addition, processing is crucial to achieve a transfer of potential HEA/MEA materials to real applications, e.g., highly stressed components. Since fusion welding is the most important joining process for metals, it is of vital importance to investigate the weldability of these materials. However, this has rarely been the subject of research to date. For that reason, in this work, the weldability depending on the surface preparation of a CoCrFeMnNi HEA and a CoCrNi MEA for TIG welding is investigated. The fusion welding of longer plates is described here for the first time for the CoCrNi alloy. The welds of both materials showed distinct formation of cracks in the heat affected Zone (HAZ). Optical and scanning electron microscopy analysis clearly confirmed an intergranular fracture topography. However, based on the results, the crack mechanism cannot be conclusively identified as either a liquid metal embrittlement (LME) or hot cracking-like liquid film separation.
Die Bestrebungen zur Verringerung der CO2-Emissionen erfordern hochbelastbare und effiziente Komponenten aus Stahl in der Anlagen-, Verfahrens- und Kraftwerkstechnik. Hierfür sind in zunehmendem Maße auf den Anwendungsfall und Stahlwerkstoff abgestimmte Verschleißschutzschich-ten und definierte, zerspante Oberflächen notwendig. Die hohen Härten dieser Schichten und der Einsatz konventioneller Co-basierter Verschleißwerkstoffe führen oftmals zu unwirtschaftlichen Bauteilen, gerade aufgrund hohen Werkzeugverschleißes bei der Zerspanung mit geometrisch bestimmter Schneide. Er-kenntnisse über den Einsatz Ni-basierter Verschleißwerkstoffe und die Optimierung der Zerspanbarkeit mittels Legierungsmodifikationen und moderner hybrider Fräsprozesse ohne Verschlechterung der Ver-schleißschutzeigenschaften sind deshalb für die Anwender und Verarbeiter zur wirtschaftlichen Fertigung hochbelasteter Stahlbauteile wesentlich. Der vorliegende Beitrag stellt die Untersuchungsmethodik eines aktuell laufenden Vorhabens der TU Clausthal und BAM, Berlin, vor. Fokus liegt hierbei auf den hochin-strumentierten Fräsexperimenten, die eine reproduzierbare Analyse und Korrelation zwischen den mik-rostrukturellen Eigenschaften der auftraggeschweißten Legierungen, dem Zerspanprozess und der Zer-spanbarkeit, insbesondere der resultierenden Oberflächenintegrität, ermöglichen sollen.
Die Verringerung der CO2-Emissionen ist eng mit der Entwicklung hocheffizienter und wirtschaftlicher Komponenten aus Stahl in der Anlagen- und Verfahrenstechnik verknüpft. Um den hohen kombinier-ten korrosiven, tribologischen, thermischen und mechanischen Beanspruchungen stand zu halten, werden auf Anwendungsfall und Stahlwerkstoff abgestimmte Verschleißschutzschichten eingesetzt. Neben der zunehmenden Forderung konventionelle Kobalt- durch Nickellegierungen zu ersetzen, wächst auch der Bedarf nach definierten Ober- bzw. Funktionsflächen hoher Güte. Aufgrund hohen Werkzeugverschleißes ist die erforderliche Fräsbearbeitung zu Herstellung der komplexen Geomet-rien der Bauteile für KMU oftmals wirtschaftlich nicht möglich. Mittels Legierungsmodifikation der Schweißzusätze für nickelbasierte plasmaauftraggeschweißte Verschleißschutzschichten und durch den Einsatz innovativer ultraschallunterstützter Fräsprozesse soll eine günstigere Zerspanbarkeit er-reicht werden, ohne das Verschleißschutzpotential zu mindern. Im vorliegenden Beitrag wird der Ein-fluss der mittels Legierungsmodifikation eingestellten Gefüge- und Ausscheidungsmorphologie auf die Zerspanbarkeit untersucht. Dies erfolgt anhand einer typischerweise für Schneckenmaschinen einge-setzten Verschleißschutzlegierung NiCrMoSiFeB-Legierung („Colmonoy 56 PTA“), die konventionelle CoCr-Legierungen (Stellite) substituiert. Metallurgische Untersuchungen und In-situ-Messungen auf-tretender Prozesskräfte an der Werkzeugschneide beim Fräsen sowie anschließende Untersuchungen von Werkzeugverschleiß und Oberflächenintegrität ermöglichen eine detaillierte Analyse und Korrela-tion zwischen mikrostrukturellen Eigenschaften und Zerspanbarkeit.
Experimentelle Charakterisierung der WIG-Schweißeignung einer Hoch- und Mittelentropie-Legierung
(2021)
Hoch- und Mittelentropie-Legierungen (engl. High/Medium Entropy Alloys–HEA/MEA) sind relativ neue Werkstoffklassen. Im Gegensatz zu herkömmlichen Legierungen bestehen HEA aus fünf bzw. MEA aus drei oder vier Legierungselementen im äquiatomaren Gleichgewicht. Um diese als reale Bauteile in die Anwendung zu überführen, muss die Verarbeitbarkeit ausführlich erforscht werden. In dieser Präsentation werden dafür erste Ergebnisse der schweißtechnischen Verarbeitung mittels WIG-Schweißen dargestellt. Dazu wurden zunächst die Schweißparameter mit einer Referenzlegierung (Ni-Basislegierung: 2.4858) bestimmt und auf eine CoCrFeMnNi-HEA sowie eine CoCrNi-MEA übertragen.
Experimentelle Charakterisierung der WIG-Schweißeignung einer Hoch- und Mediumentropie-Legierung
(2021)
Equiatomic multi-element systems with defined entropy are a relatively new mate-rial concept for alloy production. These alloys consist of at least five elements in equiatomic distribution in the case of high entropy alloys (HEA) and three to four elements in equiatomic distribution in the case of medium entropy alloys (MEA). Previous studies on these alloys have focused primarily on their production, micro-structure and the resulting material properties. Meanwhile, the focus here is on the processing of the alloys and their influence on future applications. Up to now, there has been insufficient knowledge of the materials and processes involved in weld-ing.
In this work, therefore, the weldability of a CoCrFeMnNi-HEA and a CoCrNi-MEA by means of a TIG welding process was investigated as a basic system. To this end, the welding parameters were first determined on a reference alloy (Ni-based: 2.4858) and transferred to the welding of the CoCrFeMnNi-HEA and CoCrNi-MEA. Weldability was assessed by testing the absence of defects and microstructures obtained. The weld metal exhibited the dendritic microstructure typical of TIG, with microsegregations forming as interdendritic phases. Increased hardness was de-tected in the weld metal compared to the base metal. In the heat-affected zone, there was little grain growth and, in both alloys, the formation of hot cracks after welding. The cause of the cracks was to be found in the specimen preparation, which had an influence on the subsequent processing. After elimination of this in-fluence, no welding process-related imperfections were found in the CoCrFeMnNi-HEA and CoCrNi-MEA.
In summary, both materials show good fusion weldability by TIG welding. The re-sults of this work thus contribute to the understanding of the weldability of HEA and in particular for CoCrNi-MEA, which was considered in this depth for the first time.
Experimentelle Charakterisierung der WIG-Schweißeignung einer Hoch- und Mediumentropie-Legierung
(2021)
Equiatomic multi-element systems with defined entropy are a relatively new mate-rial concept for alloy production. These alloys consist of at least five elements in equiatomic distribution in the case of high entropy alloys (HEA) and three to four elements in equiatomic distribution in the case of medium entropy alloys (MEA). Previous studies on these alloys have focused primarily on their production, micro-structure and the resulting material properties. Meanwhile, the focus here is on the processing of the alloys and their influence on future applications. Up to now, there has been insufficient knowledge of the materials and processes involved in weld-ing.
In this work, therefore, the weldability of a CoCrFeMnNi-HEA and a CoCrNi-MEA by means of a TIG welding process was investigated as a basic system. To this end, the welding parameters were first determined on a reference alloy (Ni-based: 2.4858) and transferred to the welding of the CoCrFeMnNi-HEA and CoCrNi-MEA. Weldability was assessed by testing the absence of defects and microstructures obtained. The weld metal exhibited the dendritic microstructure typical of TIG, with microsegregations forming as interdendritic phases. Increased hardness was de-tected in the weld metal compared to the base metal. In the heat-affected zone, there was little grain growth and, in both alloys, the formation of hot cracks after welding. The cause of the cracks was to be found in the specimen preparation, which had an influence on the subsequent processing. After elimination of this in-fluence, no welding process-related imperfections were found in the CoCrFeMnNi-HEA and CoCrNi-MEA.
In summary, both materials show good fusion weldability by TIG welding. The re-sults of this work thus contribute to the understanding of the weldability of HEA and in particular for CoCrNi-MEA, which was considered in this depth for the first time.
Verschleißschutz durch Hartphasenauftragschweißungen mit spanend bearbeiteten Funktionsflächen
(2022)
Das Schlichtfräsen von Verschleißschutzlegierungen ist aufgrund hohen Werkzeugverschleißes vor allem für KMU oftmals nicht wirtschaftlich. Durch gezielte Legierungsmodifikationen sowie den Einsatz hybrider Fertigungsprozesse wie dem ultraschallunterstützten Fräsen soll die Zerspanbarkeit der Legierungen verbessert werden. In dieser Präsentation werden erste Ergebnisse zu Voruntersuchungen zu der Legierung und den Einfluss auf das Werkzeug gezeigt.
Die Ziele zur Verringerung der CO2-Emissionen sind eng verknüpft mit der Entwicklung hocheffizienter und wirtschaftlicher Komponenten aus Stahl in der Anlagen-, Verfahrens- und Kraftwerktechnik, die für hohe kombinierte korrosive, tribologische, thermische und mechanische Beanspruchungen auf Anwendungsfall und Stahlwerkstoff abgestimmte Verschleißschutzschichten erfordern. Neben zunehmender Forderungen infolge des Preis- und Lieferrisikos konventionelle Kobalt- durch Nickellegierungen zu ersetzen, wächst in der Industrie der Bedarf nach definierten Oberflächen hoher Güte bzw. Funktionsflächen für die Schutzschichten. Eine für Bauteile mit komplexer Geometrie erforderliche Fräsbearbeitung ist insbesondere für KMU aufgrund hohen Werkzeugverschleißes oftmals nicht wirtschaftlich realisierbar, jedoch für viele Einsatzfälle dringend notwendig.
Es soll daher mittels Legierungsmodifikationen an Schweißzusätzen für nickelbasierte plasmaauftraggeschweißte Verschleißschutzschichten und durch Einsatz innovativer ultraschallunterstützter Fräsprozesse eine günstigere Zerspanbarkeit erreicht werden, ohne das Verschleißschutzpotential zu mindern.
Im vorliegenden Beitrag wird die Methodik für die Untersuchungen der Wechselwirkung zwischen der mittels Legierungsmodifikation eingestellten Gefüge- bzw. Ausscheidungsmorphologie und der durch Ultraschalloszillation unterstützten Zerspanungskinetik mittels hochinstrumentierter Fräsversuche vorgestellt. In-situ-Messungen auftretender Prozesskräfte (mittels Dynamometer), Oszillationen (mittels Laser-Vibrometer) und Temperaturen (mittels Hochgeschwindigkeitspyrometer) an der Werkzeugschneide sowie der anschließenden Untersuchungen von Werkzeugverschleiß und Oberflächenintegrität (Rauheit, Degradationen, fertigungsbedingte Beanspruchungen) ermöglichen eine detaillierte, reproduzierbare Analyse und Korrelation zwischen den mikrostrukturellen Eigenschaften und der Zerspanbarkeit. Unter systematischer Anwendung dieser Methodik sowie der Berücksichtigung der Anbindung zum Stahlsubstratwerkstoff und der Wirksamkeit des Verschleißschutzes lässt sich letztlich eine gezielte Optimierung der Zerspanungssituation erreichen.
Die Ziele zur Verringerung der CO2-Emissionen sind eng verknüpft mit der Entwicklung hocheffizienter und wirtschaftlicher Komponenten aus Stahl in der Anlagen-, Verfahrens- und Kraftwerktechnik, die für hohe kombinierte korrosive, tribologische, thermische und mechanische Beanspruchungen auf Anwendungsfall und Stahlwerkstoff abgestimmte Verschleißschutzschichten erfordern. Neben zunehmender Forderungen infolge des Preis- und Lieferrisikos konventionelle Kobalt- durch Nickellegierungen zu ersetzen, wächst in der Industrie der Bedarf nach definierten Oberflächen hoher Güte bzw. Funktionsflächen für die Schutzschichten. Eine für Bauteile mit komplexer Geometrie erforderliche Fräsbearbeitung ist insbesondere für KMU aufgrund hohen Werkzeugverschleißes oftmals nicht wirtschaftlich realisierbar, jedoch für viele Einsatzfälle dringend notwendig.
Es soll daher mittels Legierungsmodifikationen an Schweißzusätzen für nickelbasierte plasmaauftraggeschweißte Verschleißschutzschichten und durch Einsatz innovativer ultraschallunterstützter Fräsprozesse eine günstigere Zerspanbarkeit erreicht werden, ohne das Verschleißschutzpotential zu mindern.
This presentation summarizes the latest research results of the influence of the post weld heat treatment (PWHT) rate and
the global mechanical stress conditions on the stress relief cracking (SRC) susceptibility of low-alloyed and creep-resistant CrMoV steel submerged arc weld joints. It was found that a certain effect of very low heating rates could be confirmed. In addition, the interlinking of SRC susceptibility increasing effects during the PWHT and the ex-post indentification in metallographic cross-section via microstructure characterization is very complex.