Filtern
Dokumenttyp
- Vortrag (19)
- Zeitschriftenartikel (6)
- Beitrag zu einem Tagungsband (5)
- Buchkapitel (1)
- Posterpräsentation (1)
Schlagworte
- Additive Fertigung (18)
- Ultraschallunterstütztes Fräsen (17)
- Legierungsmodifikation (15)
- Alloy 36 (12)
- Ultrasonic-assisted milling (11)
- Surface integrity (10)
- Additive manufacturing (8)
- Alloy modification (7)
- Oberflächenintegrität (6)
- DVS (3)
- Fortschrittsbericht (3)
- Ni alloy (3)
- Plasma-transferred arc welding (3)
- Plasma-Pulver-Auftragschweißen (2)
- Werkzeugverschleiß (2)
- Co-Cr-Legierung (1)
- Co-Cr-alloy (1)
- Cobalt-chromium alloy (1)
- Contour method (1)
- DED-Arc (1)
- Eigensapnnungen (1)
- Metallschutzgasschweißen (1)
- Modification of structural morphology (1)
- Plasma-Transferred-Arc (1)
- Projektbegleitender Ausschuss (1)
- Residual stress (1)
- Schweißzusatzmodifikation (1)
- Schwer spanbar (1)
- Ultraschallunterstützter Fräsprozess (1)
- ultraschallunterstütztes Fräsen (1)
Organisationseinheit der BAM
Alloy 36 (1.3912) is an alloy with 36% nickel and 64% iron and is generally classified as a difficult-to-cut material. Increasingly complex structures and the optimization of resource efficiency are making additive manufacturing (AM) more and more attractive for the manufacture or repair of components. Subsequent machining of AM components is unavoidable for its final contour. By using modern, hybrid machining processes, e.g., ultrasonic-assisted milling (US), it is possible to improve the cutting situation regarding the resulting surface integrity as well as the cutting force. Part I deals with the influence of the alloying elements Ti, Zr, and Hf on the microstructure and the hardness of the initial alloy 36. Part II focusses on the effect of the alloy modifications and the ultrasonic assistance on machinability as well as on the surface integrity after finish-milling. The results show a highly significant influence of the ultrasonic assistance. The cutting force during the US is reduced by over 50% and the roughness of approx. 50% compared to conventional milling (CM) for all materials investigated. Moreover, the US causes a defect-free surface and induces near-surface compressive residual stresses. CM leads to a near-surface stress state of approx. 0 MPa.
Die additive Fertigung (AM) durch schweißtechnische Verfahren eröffnet vielfach ökonomische Vorteile für eine ressour-ceneffiziente Bauteilherstellung. Gerade hinsichtlich der Homogenität und Anisotropie der resultierenden Schweißgefüge und den damit verbundenen Eigenschaften gibt es noch offene Fragestellungen. Die Einstellung der finalen Bauteilgeo-metrie und Oberflächengüte erfordert den komplementären Einsatz abtragender Fertigungsschritte. Hochleistungslegie-rungen auf der Basis von Nickel oder Kobalt sind aufgrund ihrer niedrigen Wärmeleitfähigkeit verbunden mit hoher Festigkeit und Zähigkeit schwer spanbar. Eine gezielte Gefügebeeinflussung mittels Modifikation der AM-Schweißzusatz-werkstoffe und der Einsatz des ultraschallunterstützten Fräsens (US) bietet das Potential insgesamt die Zerspanungssi-tuation zu verbessern. Dieser Lösungsansatz unter Gewährleistung des Erhalts der geforderten Werkstoff- bzw. Bauteileigenschaften ist Untersuchungsgegenstand eines Gemeinschaftsvorhabens (IGF-Nr. 20.979 N/DVS-Nr. 1.3211) der BAM und TU Clausthal/ISAF. Der vorliegende Beitrag stellt Ergebnisse für die beiden untersuchten FeNi- und CoCr-Legierungen sowie wesentliche Zusammenhänge zwischen Legierungsmodifikation, entstehender Gefügemorphologie und Zerspanungseigenschaften der mittels MAG additiv gefertigter Proben vor. Das größte Potential für die Modifikation zeigten Zr und Hf. Die Zulegierung in das Schweißgut erfolgte durch Beschichtung von Massivdrähten sowie durch Her-stellung von Fülldrähten.
Die additive Fertigung mittels Schweißverfahren bietet große ökonomische Vorteile für eine ressourceneffiziente Bauteilherstellung. Offene Fragen bezüglich Homogenität, Anisotropie der Schweißgefüge und den damit verbundenen Bauteileigenschaften stehen einer wirtschaftlichen Verarbeitung oftmals im Wege. Finale Bauteilgeometrie und Oberflächengüte erfordern meist komplementäre subtraktive Fertigungsschritte. Werkstoffe für hochbelastbare Komponenten sind oftmals schwer spanbar. In einem Vorhaben der BAM und des ISAF wurde untersucht, wie die Modifikation der AM-Schweißzusätze und das ultraschallunterstützte Fräsen (US) die Zerspanungssituation verbessern. Der vorliegende Artikel stellt wesentliche Zusammenhänge zwischen Legierung, Gefüge und Zerspanung zweier schwer spanbarer Hochleistungslegierungen (FeNi und CoCr) dar. Großes Potenzial zeigte neben dem US die Modifikation mit Zr und Hf bei Zulegierung in das Schweißgut mittels Beschichtung von Massivdrähten bzw. Herstellung von Fülldrähten.
Untersuchungsmethoden beim Fräsen additiv gefertigter schwer spanbarer Kobalt-Chrom-Legierungen
(2021)
Für den Anlagenbau werden hochbelastete Komponenten aus Co-Cr-Legierungen hergestellt. Dabei ist die Zerspanung so herausfordernd, dass additive Fertigungsschritte oft wirtschaftlicher sind. Diese bedingen aber vorwiegende heterogene, anisotrope Gefüge und Eigenschaften und bei nachfolgender Fräsbearbeitung unstetige Zerspankräfte und instabile Spanvorgänge. Hierbei können hybride Zerspanprozesse helfen, hohe Belastungen für Werkzeug und Werkstückoberfläche zu minimieren. Diesbezügliche Charakterisierungen erfordern speziell adaptierte Zerspanungsanalysen.
Anhand eines Anwendungsbeispiels, bei dem eine Modifikation der Ausgangslegierung mit 1 % Hf erfolgte, wird die Wechselwirkung zwischen Gefügemorphologie und Fräsprozess dargestellt, der konventionelle mit einem hybriden ultraschallunterstützten Fräsprozess verglichen und die Charakterisierung des Werkzeugverschleißes anhand zweier verschiedener Fräser betrachtet. Analysen auftretender Prozesskräfte mittels Piezo-Mehrkomponenten-Dynamometer, der Werkzeugoszillation mittels Laser-Vibrometer und zusätzliche In-situ-Temperaturmessungen der Werkzeugschneiden mittels Highspeed-Pyrometer bilden den Kern der neuen Zerspanungsprüftechnik.
Die vorgestellten Untersuchungsmethoden bilden die Vorgänge bei der Zerspanung additiv gefertigter Werkstoffe detailliert und reproduzierbar ab. Sowohl Legierungsmodifikation als auch hybride Prozessbedingungen lassen gezielte Einflüsse zur deutlichen Verbesserung der Zerspanungssituation zu.
Ni alloys are generally classified as difficult-to-cut materials and cost intensive. Additive manufacturing (AM) offers economic advantages. However, machining of these AM components is mandatory to create the final contour or surface. The inhomogeneous and anisotropic microstructure and properties of AM components causes an unstable cutting process. Moreover, undesirable tensile residual stresses are generated due to subsequent machining. In this investigation, the initial alloy 36 is modified with Ti and Nb up to 1.6 wt.-% and build-up welded via gas metal arc welding (GMAW) and plasma-transferred-arc (PTA). Then, finish-milling tests are carried out to investigate the influence of the modification as well as the cutting parameters on the resulting cutting force and the surface integrity. In addition, the conventional milling process (CM) is compared with the ultrasonic-assisted milling process (US), which has a significant influence on the machinability as well as on the surface integrity.
Nickel alloys are cost intensive materials and generally classified as difficult-to-cut material. However, machining of these materials is needed especially in case of alloy 36 (1.3912), which is commonly used in mould construction for the production of fibre-reinforced composites. With regard to repair, modification and manufacturing of such components, additive manufacturing offers significant economic advantages. Nevertheless, subsequent machining steps are needed to achieve the final component contour and defined surface conditions. Dependent on the material and machining process conditions, detrimental tensile residual stresses may be the result on the machined surface, having negative impact on the component performance and safety. In this investigation, machining experiments were carried out on wire arc additive manufactured components made of alloy 36, varying the cutting speed and the feed rate. In addition, the conventional milling process (CM) was compared with a modern, hybrid machining process, the ultrasonic-assisted milling (US). The cutting forces and the surface-near residual stresses were analysed using X-ray diffraction. A significant improvement of the machinability as well as the surface integrity by using the ultrasonic assistance was observed, especially at low cutting speeds. The CM induced mainly tensile residual stresses, the US mainly compressive residual stresses.
Das DVS-Vorhaben 01.3211 „Herstellung beanspruchungsgerechter Oberflächen durch Kombination innovativer additiver und abtragender Fertigungsschritte an hochbelasteten Komponenten“ ist ein Kooperationsprojekt der Bundesanstalt für Materialforschung und -prüfung (BAM) und dem Institut für Schweißtechnik und Trennende Fertigungsverfahren (ISAF) der Technischen Universität Clausthal. Das Übergeordnete Projektziel ist das Erlangen von Erkenntnissen für eine sichere und wirtschaftliche, kombinierte additive und abtragende Fertigung aus kostenintensiven Werkstoffen hochbelasteter Komponenten insbesondere für KMU. Dabei stehe die beiden Werkstoffe CoCr26Ni9Mo5W (2.4681) und FeNi36 (1.3912) im Fokus. Mittels Modifikation der Schweißzusätze sind homogen und isotrop ausgeprägte Werkstoffeigenschaften und eine Erhöhung der Prozessstabilität und Fertigungsfreiheitsgrade bei der additiven Fertigung erzielbar. Darüber hinaus wird der Einfluss nachfolgender abtragender Bearbeitungsschritte des ultraschallunterstützen und des konventionellen Fräsprozesses untersucht. Im Laufe der Sitzung des projektbegleitenden Ausschusses (PbA) wurde der aktuelle Bearbeitungsstand sowie der Zeitplan vorgestellt. Darüber hinaus wurde mit dem PbA über die bereits erzielten Ergebnisse diskutiert. Abschließend wurde ein kurzer Ausblick über die zeitnah beginnenden Arbeiten beider Forschungseinrichtungen sowie ein Überblick über die vorhabenbezogenen Aufwendungen der Wirtschaft und des Ergebnistransfers in die Wirtschaft gegeben.
Zunächst wird die BAM vorgestellt. Anschließend wird die Messung bzw. Bestimmung der Amplitude der Ultraschallunterstützung erläutert, gefolgt von Schlichtfräsexperimenten an AM-Bauteilen aus einer schwer spanbaren FeNi-Legierung. Es werden die Ergebnisse der Zerspankraft, der Rauheit und der Eigenspannungen vorgestellt.
Für den Anlagenbau werden hochbelastete Komponenten aus Co-Cr-Legierungen hergestellt. Dabei ist die Zerspanung so herausfordernd, dass additive Fertigungsschritte oft wirtschaftlicher sind. Diese bedingen aber vorwiegende heterogene, anisotrope Gefüge und Eigenschaften und bei nachfolgender Fräsbearbeitung unstetige Zerspankräfte und instabile Spanvorgänge. Hierbei können hybride Zerspanprozesse helfen, hohe Belastungen für Werkzeug und Werkstückoberfläche zu minimieren. Diesbezügliche Charakterisierungen erfordern speziell adaptierte Zerspanungsanalysen.
Anhand eines Anwendungsbeispiels, bei dem eine Modifikation der Ausgangslegierung mit 1 % Hf erfolgte, wird die Wechselwirkung zwischen Gefügemorphologie und Fräsprozess dargestellt, der konventionelle mit einem hybriden ultraschallunterstützten Fräsprozess verglichen und die Charakterisierung des Werkzeugverschleißes anhand zweier verschiedener Fräser betrachtet. Analysen auftretender Prozesskräfte mittels Piezo-Mehrkomponenten-Dynamometer, der Werkzeugoszillation mittels Laser-Vibrometer und zusätzliche In-situ-Temperaturmessungen der Werkzeugschneiden mittels Highspeed-Pyrometer bilden den Kern der neuen Zerspanungsprüftechik.
Die vorgestellten Untersuchungsmethoden bilden die Vorgänge bei der Zerspanung additiv gefertigter Werkstoffe detailliert und reproduzierbar ab. Sowohl Legierungsmodifikation als auch hybride Prozessbedingungen lassen gezielte Einflüsse zur deutlichen Verbesserung der Zerspanungssituation zu.
Ni alloys are cost intensive materials and generally classified as difficult-to-cut materials. However, machining of these materials is needed especially in case of alloy 36 (1.3912), which is commonly used in mould construction for the production of fibre-reinforced composites. With regard to repair, modification and manufacturing of such components, additive manufacturing offers significant economic advantages. Nevertheless, subsequent machining steps are needed to achieve the final component contour and defined surface conditions. Dependent on the material and machining process conditions, detrimental tensile residual stresses may be the result on the machined surface, having negative impact on the component performance and safety. Recent studies exhibited that hybrid machining processes, such as ultrasonic-assisted milling (USAM), are suitable for achieving favourable residual stress states at the surface of difficult-to-cut Ni-Cr alloys. In this investigation, wire arc additive manufactured (WAAM) specimens of alloy 36 were finish milled under different milling conditions. In addition to the machined surfaces condition and topology, the surface-near residual stresses were analysed using X-ray diffraction (XRD). Especially for low cutting speeds, significantly improved surface properties, roughness parameters and lower mechanical and microstructural degradations were found for the specimen machined with USAM compared to conventional milling. The improved surface integrity could furthermore be observed by a significant reduction of the tensile residual stresses in the surface boundary area.