We report on the development of a field-proven distributed fiber optic sensing system for structural health monitoring in road construction and civil engineering. The system is based on a cost-efficient digital incoherent optical frequency domain reflectometry (I-OFDR) for distributed strain detection along a polymer optical fiber. In this method, the strain-induced backscatter increase in a graded-index multimode perfluorinated polymer optical fiber (PF-POF) is determined by measuring the complex transfer function of the sensing fiber using a compact digital data acquisition unit.
The sensitivity of low-loss perfluorinated polymer optical fiber (PF-POF) to gamma radiation is investigated for on-line radiation monitoring purposes. The radiation-induced attenuation (RIA) of a commercial PF-POF based on Cytop material is measured in the visible spectral region. The fiber RIA shows strong wavelength dependence with rapid increase towards the blue side of the spectrum. The wide range of radiation sensitivities is available via careful selection of appropriate monitoring wavelength. The accessible sensitivities span from 1.6 ± 0.2 dBm-1/kGy measured at 750 nm to 18.3 ± 0.7 dBm-1/kGy measured at 420 nm. The fairly high radiation sensitivity as well as its wide tunability makes the fiber a promising candidate for a broad range of applications.
In this paper, we present the first results regarding the on-line monitoring of gamma-ray exposure effects on a commercial multi-mode perfluorinated polymer optical fiber (PF-POF), type GigaPOF-50SR from Chromis Fiberoptics. Our focus was to evaluate on-line the radiation induced attenuation (RIA) over a wide spectral range (320 nm – 1700 nm), in order to assess the fiber’s radiation hardness and its possible use in radiation detection. An Ocean Optics QE65000 high sensitivity spectrometer and a StellarNet near-IR spectrometer were used to cover the spectral ranges 200 nm – 1μm and 900 nm – 1.6 μm, respectively. Electron paramagnetic resonance was used to monitor the recovery of the irradiation induced centers at room temperature. The study indicated that the optical fiber can be used as radiation monitor at low dose rates by measuring the attenuation in the UV, while higher dose rates irradiation can be observed by RIA monitoring at specific wavelengths in the visible spectral range.
In this work, the potential of fiber Bragg gratings (FBGs) in low-loss perfluorinated polymer optical fibers (PF-POFs) is explored. The FBG is femtosecond-inscribed in a commercial multi-mode (MM) PF-POF based on Cytop® polymer. Femtosecond inscription leads to creation of a highly saturated grating with a number of higher order reflection Peaks visible throughout the visible and near-infrared spectral region. For 2 mm long FBG having a pitch of 2.2895 μm, a total of nine higher-order MM reflection bands are visible spanning from 1548 nm (4th order) to 520 nm (12th order). Strain sensitivity was measured for 6 peak bands in 500-900 nm region, where relatively low cost CCD based spectrometers and broadband LEDs are available. Strain sensitivity increases almost linearly with increasing initial peak wavelength, growing from 4.82 ± 0.02 nm/% measured for 12th order peak at 517 nm to 8.12 ± 0.04 nm/% measured for 7th order peak at 883 nm. These values correspond to roughly 20 % higher sensitivity than silica FBGs exhibit in this spectral range. The gratings in PF-POFs combine the higher strain sensitivity and low-loss operation while maintaining the mechanical advantages of polymer optical fibers. Therefore, they hold a high potential for considerable broadening of polymer optical fiber Bragg gratings application range.