Filtern
Dokumenttyp
- Vortrag (9)
- Posterpräsentation (4)
- Zeitschriftenartikel (3)
- Beitrag zu einem Tagungsband (1)
Sprache
- Englisch (17) (entfernen)
Schlagworte
- Microbiologically influenced corrosion (17) (entfernen)
Organisationseinheit der BAM
- 4 Material und Umwelt (12)
- 4.1 Biologische Materialschädigung und Referenzorganismen (12)
- 6 Materialchemie (6)
- 6.2 Material- und Oberflächentechnologien (6)
- 1 Analytische Chemie; Referenzmaterialien (4)
- 1.1 Anorganische Spurenanalytik (4)
- 9 Komponentensicherheit (1)
- 9.0 Abteilungsleitung und andere (1)
Eingeladener Vortrag
- nein (9)
Microbiologically influenced corrosion (MIC) is a highly unpredictable process involving a complex group of microorganisms, including sulfate-reducing bacteria and methanogens. Standard laboratory MIC testing using static serum bottle enrichments is an easy but limited method, offering poor resolution on the biomineralization process of corrosion products. An example of this is the presumed corrosion product siderite by corrosive methanogens (Mi-MIC). Previous publications reported siderite was the sole corrosion product of M. maripaludis using metal coupons incubated under stationary conditions.
However, the formation of siderite is closely related to the surrounding environmental conditions, i.e. pH, CO2 concentration, flow and temperature. Thus, siderite as the sole corrosion product of Mi-MIC remain inconclusive and questionable. To study Mi-MIC effectively, a novel versatile multiport flow-column corrosion monitoring system (MFC) was developed. MFC allows sectional corrosion rate determination under flow conditions using different types of material, inoculum and packing material. MFC offers great flexibility, ease of operation and accurate corrosion measurements that can be combined with many other techniques. Using MFC, we studied multiple strains of methanogens and compared it with sulfate-reducing bacteria under neutral and low pH conditions. It was revealed by MFC that corrosive methanogens have equally high corrosion potential as sulfate-reducing bacteria. Additionally, siderite is not the dominant nor sole corrosion product of Mi-MIC. Thus, effective corrosion monitoring and establishing standard laboratory practices, i.e. incorporating MFC as part of regular testing process, will provide deeper understanding of MIC. This will allow further microbial electrophysiology understandings, contributing to effective mitigation strategy development.
Microbiologically influenced corrosion (MIC) of iron is usually attributed to sulfate-reducing microorganisms (SRM) in oil and gas facilities. SRM act upon the metal by the re-activeness of hydrogen sulfide (HS-), and by withdrawal of the available electrons in electrical contact with the metal (EMIC). Methanogenic archaea (MA) can also cause MIC (Mi-MIC). Several MAs were identified to be corrosive by using elemental iron as the sole electron donor for methanogenesis, including Methanobacterium-affliated IM1 and Methanococcus maripaludis Mic1c10. Currently, low corrosion rates were reported for MA, possibly due to the formation of siderite (4Fe + 5HCO3- + 5H+ ® 4FeCO3 + CH4 + 3H2O). Since MA do not produce HS-, withdrawal of electrons may be their main corrosive mechanism; however, mechanistic details and kinetics of the overall process are poorly understood.
To investigate the corrosion potential of MA, we studied the EMIC methanogenic strains (IM1 and Mic1c10) individually or part of a syntrophic co-culture with SRM. Corrosion studies were conducted using an in-house developed flow-through system to simulate fluctuating environmental conditions. Results indicate that the rates of iron corrosion by MA (up to 0.4 mm/yr) are higher to that caused by the marine SRM Desulfovibrio alaskensis (0.15 mm/yr) and the co-culture (0.1 mm/yr). Scanning electron microscopy (SEM) images of the metal incubated with MA showed severe pitting corrosion. Genomic analysis of the EMIC MA was conducted to provide an insight on the possible cellular mechanisms that could be involved. Furthermore, low concentrations of MA-targeting biocides will be applied to EMIC MA in static and flow conditions to gain insights for possible mitigation strategies. Such knowledge and deeper understanding also from an electrokinetic point of view may not only provide further models in microbial electrophysiology, but also contribute to mitigation strategies in MIC.
With the latest ICP-MS technology - ICP-ToF (time of flight)-MS - it is possible to analyze the multi-element fingerprint of individual cells. The interface between material and environmental analysis thus receives special attention, e.g. when considering corrosion processes. Microbiologically influenced corrosion (MIC) is highly unpredictable due to the diversity of microbial communities involved. The development of the MIC-specific ICP-ToF-MS analytical method presented here at the single cell level, in combination with the investigation of steel-MIC interactions, contributes significantly to progress in instrumental MIC analysis and will enable clarification of the processes taking place.
The supplied document shows the basis of a four minutes lightning talk.
ICP-ToF (Flugzeitanalysator, engl. time of flight)-MS ermöglicht den Multielement Fingerabdruck einzelner Zellen (single cell) zu analysieren. Die single cell-ICP-ToF-MS kommt bei dem vorgestellten Poster bei der Analyse von Archaeen, die an mikrobiell beeinflusster Korrosion (engl. microbiologically influenced corrosion, MIC) von Stahl eine Rolle spielen, zum Einsatz. Mittels sc-ICP-ToF-MS wird die mögliche Aufnahme von einzelnen Elementen aus dem jeweiligen Stahl untersucht – die erhaltenen Informationen fließen zukünftig in die Aufklärung zugrunde liegender Mechanismen sowie Entwicklung möglicher Materialschutzkonzepte ein. Die Arbeiten Verknüpfen moderne Methoden der Analytical Sciences mit Materialien.
ICP-ToF (time of flight) MS enables the analysis of the multi-element fingerprint of single cells. The single cell ICP-ToF-MS is used in the presented poster for the analysis of archaea involved in microbiologically influenced corrosion (MIC) of steel. By means of sc-ICP-ToF-MS, the possible uptake of individual elements from the respective steel is investigated - the information obtained will be used in the future to elucidate underlying mechanisms and develop possible material protection concepts. The work combines modern methods of analytical sciences with materials.
Currently, corrosion rates (CR) and/or corrosion products (CP) obtained for methanogen-induced microbiologically influenced corrosion (Mi-MIC) on carbon steel are mainly analyzed from static-incubations. By using a multiport-flow-column, much higher CRs (0.72 mm/yr) were observed, indicating static-incubations are not suitable for determining the corrosive potential of Mi-MIC. With the combination of various analytical methods (ToF-SIMS/SEM-EDS/SEM-FIB) and contrary to previously published data, we observed that CPs contained phosphorus, oxygen, magnesium, calcium and iron but lacked carbon-related species (e.g. siderite). Overall, siderite nucleation is disrupted by methanogens, as they convert aqueous bicarbonate into carbon dioxide for methanogenesis resulting in increased localized corrosion.
The corrosion of stainless steel components is a problem of global scale, economically as well as in regards to the safety of industrial equipment and facilities. With microorganisms involved (microbial influenced corrosion, MIC), the problem becomes more complex. Iron reducing bacteria (IRB) for example accelerate the corrosion of iron based materials like stainless steel via the reduction of iron oxides in the passive layer. When co-cultivated with iron oxidizing bacteria, IRBs can induce deep, heterogeneously distributed pits on stainless steel surfaces. The analysis of localized corrosion – or pitting corrosion – is of great relevance since it can lead to unpredictable material failure. In general, macroscopic electrochemical methods are not capable of providing information about the spatial heterogeneity of a sample and thus need to be complemented by multi-electrode based techniques or scanning electrochemical methods.
The aim of this work is to develop methods for the analysis of localized corrosion, on stainless steel surfaces induced by IRB biofilms. The greatest challenge is to address the complexity of two heterogeneous systems at the metal/biofilm interface. First there is the variation in the passive layer composition and microstructure. Secondly, the microbial biofilm with its heterogeneous tree-dimensional structure resulting in local differential aeration cells and electrochemical parameters. To be able to differentiate between individual effects, artificial biofilms mimicking the physical properties of a natural biofilm are used in this study as model systems. This artificial biofilm is applied on a multi-electrode probe to identify local anodic sites during exposure experiments. The detailed analysis of active sites by means of scanning electrochemical microscopy (SECM) allows the investigation of local properties within the biofilm and its immediate vicinity.
The presented analytical approach delivers promising results in clarifying how localized corrosion of stainless steels develops chronologically and spatially in the presence of IRBs. Furthermore, our results on model systems provide the basis for the application of the methodology for the investigation of natural or multi-species biofilms in the future.
MFC was used to study the corrosiveness of iron-utilizing methanogen, Methanobacterium IM1 under flow conditions. Comparing against electrical SRM, Desulfovibrio ferrophilus IS5, results showed under standard mesophilic conditions, average corrosion rates of Methanobacterium IM1 was double that of SRM. The highest corrosion rate of Methanobacterium IM1 reached up to 0.60 mm/yr under neutral conditions, and severe pitting was observed on the iron surface. Furthermore, the corrosion products of Methanobacterium IM1 were characterized with TOF-SIM, FIB-SEM and EDX, and preliminary results revealed FeCO3 is not the only corrosion product of Mi-MIC, as previously reported. Under low pH conditions, the maximum corrosion rate of Methanobacterium IM1 reached 1.57 mm/yr, which resulted in severed deformity of the iron specimen. Additional comparisons using different types of incubation material were conducted to standardize MFC MIC testing.
Microbiologically influenced corrosion (MIC) is an expensive but unpredictable problem for the industries. The most well-known culprit for MIC is the sulfate-reducing microorganisms (SRM), such as members from the genus Desulfovibrio. It has been widely accepted that SRM can contribute significantly to MIC through the production of hydrogen sulfide (HS-) or in some cases a direct electron uptake from the metal surface. However, in a real environmental system, SRM is not exclusive and often involved with other microorganisms that may also contribute to MIC, such as methanogens.
Methanogenic archaea can produce methane (CH4) using H2+CO2, formate, methylated amines or acetate. Methanogens are highly abundant in the environment and many are found in very extreme conditions, such as high temperature and high salinity. Previous researches have demonstrated that methanogens are capable of MIC, though the specific mechanisms are still under investigation. In the oil and gas industry, methanogens are not considered as the main contributor for MIC since the corrosion rates are often too low. However, the tests for methanogen-induced MIC are usually performed at static conditions, which cannot represent the system accurately. Here, we developed a novel anaerobic system to evaluate the corrosion potential of methanogens under flow conditions. We will use the Methanococcus maripaludis KA1 strain, which was isolated from a crude oil tank, as the organism of interest. A separate system for Desulfovibrio alaskensis will be established for corrosion rate comparisons. Furthermore, we will study the synergistic effects of M. maripaludis and D. alaskensis on MIC under flow.
The latest ICP-MS technology - ICP-ToF (time of flight)-MS – enables the analysis of the multi-element fingerprint of individual cells. The interface between material and environmental analysis thus receives special attention, e.g., when considering corrosion processes. Microbiologically influenced corrosion (MIC) is a highly unpredictable phenomenon due to the influence of the environment, microbial communities involved and the respective electron source. However, the interaction pathway between cells and the metal surface remains unclear. The development of the MIC-specific ICP-ToF-MS analytical method presented here at the single cell level, in combination with the investigation of steel-MIC interactions, contributes significantly to progress in instrumental MIC analysis and will enable clarification of the processes taking place. For this, a MIC-specific staining procedure was developed. It allows the analysis of archaea at a single cell level and provides information about the interaction of the cells with the staining agent which is extremely scarce compared to other well characterized organisms. Additionally, the single cell ICP-ToF-MS is used for the analysis of archaea involved in MIC of steel. Hence, the possible uptake of individual elements from different steel samples is investigated - the information obtained will be used in the future to elucidate underlying mechanisms and develop possible material protection concepts, thus combining modern methods of analytical sciences with materials.