Improving the chipping resistance of pre-sintered zirconia white-bodies

  • Objectives: The high occurrence of fractures, cracking and chipping of zirconia pre-sintered blanks and blocks during machining decreases their yield and can transfer lifetime-limiting racks to the final sintered restoration. This study has the objective of characterizing the mechanical and fracture properties of two zirconia compositions while varying temperature and time of pre-sintering, in order to assess the space for possible improvement. Methods: We selected two typical granular powders with 3 mol% (3YSZ, Zpex®, Tosoh) or 5 mol% (5YSZ, Zpex Smile®, Tosoh) yttria-stabilized zirconia and two pre-sintered commercial analogs (IPS e.max® ZirCAD MO, Ivoclar and Katana™ STML, Kuraray). The debinding and pre-sintering stages of the experimental powders were characterized using thermal analyses (differential scanning calorimetry and thermogravimetry), and the crystal phase composition was quantified using X-ray diffraction (XRD). Physical and mechanical properties such as density,Objectives: The high occurrence of fractures, cracking and chipping of zirconia pre-sintered blanks and blocks during machining decreases their yield and can transfer lifetime-limiting racks to the final sintered restoration. This study has the objective of characterizing the mechanical and fracture properties of two zirconia compositions while varying temperature and time of pre-sintering, in order to assess the space for possible improvement. Methods: We selected two typical granular powders with 3 mol% (3YSZ, Zpex®, Tosoh) or 5 mol% (5YSZ, Zpex Smile®, Tosoh) yttria-stabilized zirconia and two pre-sintered commercial analogs (IPS e.max® ZirCAD MO, Ivoclar and Katana™ STML, Kuraray). The debinding and pre-sintering stages of the experimental powders were characterized using thermal analyses (differential scanning calorimetry and thermogravimetry), and the crystal phase composition was quantified using X-ray diffraction (XRD). Physical and mechanical properties such as density, hardness, flexural modulus, biaxial flexural strength and fracture toughness were measured for two pre-sintering temperatures (1000 ◦C, 1100 ◦C) and increasing holding times at those temperatures (2 h, 4 h, 6 h). The chipping resistance for those conditions was quantified using the edge chipping test using a Vickers diamond indenter. Results: Thermal analyses revealed that both powders show comparable debinding behavior and contained approx. 3.8 mass % organic binder, which burns-out completely between 300 and 400 ◦C. The crystallographic phase changes occurring during the 2–6 h at 1000 ◦C and 1100 ◦C was not detectable in the DSC signal, but quantifiable by XRD. Namely, a major content of monoclinic phase in both powders transforms completely into the two tetragonal phases, starting below 1000 ◦C and concluding above 1100 ◦C. All physical and mechanical properties increased with holding time for both temperatures, though more steeply for pre-sintering at 1100◦C. Edge chipping resistance response was well aligned with other fracture properties, with a more marked improvement for 3YSZ pre-sintered at 1100 ◦C. For all properties, the 3YSZ zirconia showed statistically-higher values for the same temperature-time conditions, in agreement with the values obtained for the commercial materials as well. Significance: The results demonstrate the weakness of pre-sintered zirconia products concerning fracture properties, but also the potential for improvement as related to type of zirconia and pre-sintering conditions. This study outlines the use of a set of mechanical tests that can characterize chipping resistance and guide future research engaging in optimizing the machining resistance of pre-sintered zirconia products.zeige mehrzeige weniger

Volltext Dateien herunterladen

Metadaten exportieren

Weitere Dienste

Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Renan BelliORCiD, Sabine Hartmann, Julia Lubauer, Raíssa Monteiro PereiraORCiD, Katrin HurleORCiD, Ling Yin, Björn MiellerORCiD, Ulrich LohbauerORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Dental Materials
Jahr der Erstveröffentlichung:2025
Organisationseinheit der BAM:5 Werkstofftechnik
5 Werkstofftechnik / 5.4 Multimateriale Fertigungsprozesse
Veröffentlichende Institution:Bundesanstalt für Materialforschung und -prüfung (BAM)
Verlag:Elsevier Inc.
Erste Seite:1
Letzte Seite:12
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Dental materials; Fracture; Pre-sintering; White body; Zirconia
Themenfelder/Aktivitätsfelder der BAM:Material
Material / Degradationsmechanismen
DOI:10.1016/j.dental.2025.12.012
URN:urn:nbn:de:kobv:b43-653457
ISSN:0109-5641
Verfügbarkeit des Dokuments:Datei für die Öffentlichkeit verfügbar ("Open Access")
Lizenz (Deutsch):License LogoCreative Commons - CC BY - Namensnennung 4.0 International
Datum der Freischaltung:14.01.2026
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:14.01.2026
Schriftenreihen ohne Nummerierung:Wissenschaftliche Artikel der BAM
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.