Synthesis and physicochemical characterization of a novel bismuth silicate templated by tetrapropylammonium bromide and polydiallyldimethylammonium chloride

  • A bismuth silicate (BiSi-1) was hydrothermally synthesized using tetrapropylammonium bromide (TPA·Br) as the organic structure-directing agent and shown by multi-scale characterization to be distinct from known Bi–silicates. Powder X-ray diffraction is indexable with an orthorhombic metric (a = 23.234 Å, b = 17.109 Å, c = 3.897 Å), consistent with a highly anisotropic, possibly layered framework. High-resolution TEM/SAED reveals nanocrystalline, plate-like domains assembled into sub-micrometric aggregates with locally oriented lamellae; lattice fringes (0.27–0.32 nm) match the strongest XRD spacings. Solid-state NMR establishes a silica-rich network with a dominant Q4 population (77%) and minor Q3 (11%) and Q2 (12%) sites; the contact-time dependence of 1H to 29Si cross-polarization is consistent with increasing proximal-proton density from Q4 to Q2. Aging to 24 h sharpens the 29Si lineshape, while calcination progressively removes the OSDA and vicinal hydroxyls; at 750 °C, 29SiA bismuth silicate (BiSi-1) was hydrothermally synthesized using tetrapropylammonium bromide (TPA·Br) as the organic structure-directing agent and shown by multi-scale characterization to be distinct from known Bi–silicates. Powder X-ray diffraction is indexable with an orthorhombic metric (a = 23.234 Å, b = 17.109 Å, c = 3.897 Å), consistent with a highly anisotropic, possibly layered framework. High-resolution TEM/SAED reveals nanocrystalline, plate-like domains assembled into sub-micrometric aggregates with locally oriented lamellae; lattice fringes (0.27–0.32 nm) match the strongest XRD spacings. Solid-state NMR establishes a silica-rich network with a dominant Q4 population (77%) and minor Q3 (11%) and Q2 (12%) sites; the contact-time dependence of 1H to 29Si cross-polarization is consistent with increasing proximal-proton density from Q4 to Q2. Aging to 24 h sharpens the 29Si lineshape, while calcination progressively removes the OSDA and vicinal hydroxyls; at 750 °C, 29Si spectra indicate framework densification/rearrangement. XANES/EXAFS places bismuth predominantly as Bi3+ in an oxide-like environment with a pronounced Bi–O first shell and no detectable Bi⁰ or Bi–Br contributions. ICP–OES yields a reproducible Bi/Si atomic ratio of 1:3. Thermogravimetry shows stepwise desorption, dehydroxylation, and template removal, with thermal stability maintained to 750 °C. Nitrogen sorption confirms mesoporosity in the as-made and Soxhlet-extracted solids (the latter exhibiting the highest surface area), whereas high-temperature calcination reduces porosity. Collectively, BiSi-1 emerges as a nanocrystalline, anisotropic Bi–silicate whose connectivity, local Bi–O environment, and accessible texture are tunable by aging and post-treatments, positioning it as a promising platform for heterogeneous catalysis and environmental remediation.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • cancella25jMatSci_Bi_silicate.pdf
    eng

Metadaten exportieren

Weitere Dienste

Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Erick Paiva Cancella, Guilherme de Paula Guarnieri, Nader de Sousa AmadeuORCiD, Martin RadtkeORCiD, Rodrigo Henrique Garcia, Eduardo Ribeiro de Azevedo, Ivana Conte Cosentino, Yvonne Primerano Mascarenhas, José Geraldo NeryORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Journal of Materials Science
Jahr der Erstveröffentlichung:2025
Organisationseinheit der BAM:6 Materialchemie
6 Materialchemie / 6.3 Strukturanalytik
Verlag:Springer Science and Business Media LLC
Jahrgang/Band:60
Ausgabe/Heft:45
Erste Seite:22615
Letzte Seite:22635
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:29Si NMR; Bismuth; Silicate
Themenfelder/Aktivitätsfelder der BAM:Material
Material / Materialdesign
DOI:10.1007/s10853-025-11732-6
ISSN:0022-2461
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:19.11.2025
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:19.11.2025
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.