The effect of humidity on the initial oxidation of the refractory high-entropy superalloy AlMo0.5NbTa0.5TiZr

  • Unlike conventional alloys, which typically consist of one main element, high-entropy alloys (HEAs) contain five or more principal elements. When compared with conventional alloys, HEAs may possess desirable properties such as improved strength/hardness, remarkable wear resistance, high structural stability, and notable oxidation resistance. However, due to the numerous possibilities of alloy composition, only a small fraction of HEAs has been characterized in terms of their mechanical and chemical properties. A refractory high-entropy superalloy AlMo0.5NbTa0.5TiZr, with its superalloy-like microstructure, belongs to the first group of a subclass of such Al-containing refractory HEAs that has recently drawn attention. The alloy has a nanoscale microstructure consisting of B2 and bcc phases, enabling high-temperature compressive strengths beyond conventional Ni-based alloys. This feature could improve turbine efficiency in the aerospace and power production industries. However, theUnlike conventional alloys, which typically consist of one main element, high-entropy alloys (HEAs) contain five or more principal elements. When compared with conventional alloys, HEAs may possess desirable properties such as improved strength/hardness, remarkable wear resistance, high structural stability, and notable oxidation resistance. However, due to the numerous possibilities of alloy composition, only a small fraction of HEAs has been characterized in terms of their mechanical and chemical properties. A refractory high-entropy superalloy AlMo0.5NbTa0.5TiZr, with its superalloy-like microstructure, belongs to the first group of a subclass of such Al-containing refractory HEAs that has recently drawn attention. The alloy has a nanoscale microstructure consisting of B2 and bcc phases, enabling high-temperature compressive strengths beyond conventional Ni-based alloys. This feature could improve turbine efficiency in the aerospace and power production industries. However, the microstructure has been reported to be sensitive to heat treatment after which it loses mechanical performance when the intragranular hexagonal Al-Zr-based intermetallic forms. This might be connected with the phase stability in the material. Then again, the addition of Al has been reported to improve the oxidation resistance of the material, but also that HEA materials tend to show pronounced zones of internal aging caused by diffusion during oxidation. These previous results imply that further research on the thermodynamic stability of the alloy is required. Furthermore, the oxidation behavior (both external and internal) and the role of humidity in the process are not fully understood. With such a multi-component material, the grain boundaries are expected to play a key role in the oxidation process, serving as short-circuit pathways for diffusion. To shed more light on the oxidation behavior of the AlMo0.5NbTa0.5TiZr alloy, experiments were carried out for 24 hours at 800 °C under both dry (21% O2 + 79% N2) and humid (8% O2 + 74% N2 + 18% H2O) atmospheres. After the experiments, the samples were characterized with XRD, SEM-EDS, and EPMA. The alloy oxidized rapidly under both studied atmospheres, resulting in a visibly oxidized region with a thickness of around 1.5 microns (dry) and 3.8 microns (humid). The porosity of the oxidized regions differs from one another: a thin layer of pores was detected in the outermost part of the oxidized zone under dry conditions, whereas the pores were distributed throughout the oxidized zone under humid conditions. Furthermore, the presence of humidity affected the phase formation. The grain boundaries, while still recognizable, differed visually from the grains in the as-received material, indicating the active role of grain boundaries during the oxidation. In addition, in the exposed samples, cracks along the grain boundaries were detected. Interestingly, cracks were also located within the grains. This could originate from the diffusion of species from the grains to the grain boundaries, which has changed the composition of grains. As a consequence, cracks formed most likely during cooling due to the Pilling-Bedworth effect. The formation of cracks suggested that the macro-scale homogeneity of the material may change during operation at high temperatures due to the active grain boundaries.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Dechema - Effect of humidity on oxidation of the HEASuperalloy.pdf
    eng

Metadaten exportieren

Weitere Dienste

Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Juho Lehmusto
Koautor*innen:Patricia Suárez Ocano, Anna Maria ManzoniORCiD, Axel KranzmannORCiD, Rene Hesse, Leonardo Agudo JácomeORCiD
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2023
Organisationseinheit der BAM:5 Werkstofftechnik
5 Werkstofftechnik / 5.1 Mikrostruktur Design und Degradation
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Grain boundaries; High-Entropy superalloy; High-Temperature Performance; Microstructure Evolution; Oxidation behavior
Themenfelder/Aktivitätsfelder der BAM:Material
Material / Degradationsmechanismen
Veranstaltung:High Temperature Corrosion and Oxidation 2023 Workshop
Veranstaltungsort:Marktheidenfeld, Germany
Beginndatum der Veranstaltung:25.09.2023
Enddatum der Veranstaltung:29.09.2023
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:06.08.2025
Referierte Publikation:Nein
Eingeladener Vortrag (wissenschaftliche Konferenzen):Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.