Brittle failure of spent fuel claddings under long-term dry interim storage conditions – Preliminary analysis

  • The evaluation of cladding integrity is a major issue to be demonstrated in Germany for extended interim storage periods up to 100 years and subsequent transportation considering operational and accidental conditions with respect to reactor operation, cask drying and dry interim storage. The chemical reaction between the zirconium fuel cladding and the cooling water in water-cooled reactors produces hydrogen and zirconium oxide. Hydrogen diffuses into the cladding and precipitates as zirconium hydrides when the solubility limit is reached, preferably oriented in hoop direction. At high temperatures during vacuum drying procedures, the hydrides can dissolve. Over a succeeding period of slow cooling with existing hoop stress the hydrides precipitate again, but partly reoriented along the radial direction of the cladding. This change of microstructure in combination with a decreasing temperature (0.5...2 K/year) during (extended) interim storage and additional mechanical load by handlingThe evaluation of cladding integrity is a major issue to be demonstrated in Germany for extended interim storage periods up to 100 years and subsequent transportation considering operational and accidental conditions with respect to reactor operation, cask drying and dry interim storage. The chemical reaction between the zirconium fuel cladding and the cooling water in water-cooled reactors produces hydrogen and zirconium oxide. Hydrogen diffuses into the cladding and precipitates as zirconium hydrides when the solubility limit is reached, preferably oriented in hoop direction. At high temperatures during vacuum drying procedures, the hydrides can dissolve. Over a succeeding period of slow cooling with existing hoop stress the hydrides precipitate again, but partly reoriented along the radial direction of the cladding. This change of microstructure in combination with a decreasing temperature (0.5...2 K/year) during (extended) interim storage and additional mechanical load by handling procedures or under accident conditions could lead to a potential cladding embrittlement and consequently increased failure probability. The current research project BRUZL (Fracture mechanical analysis of spent fuel claddings under long-term dry interim storage conditions) has been launched by BAM to investigate potential sudden brittle failure of spent fuel claddings at small deformation under long-term dry interim storage conditions and is presented.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Zencker IAEA CN-272-49 Poster.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Uwe Zencker
Koautor*innen:Kai Simbruner, Holger Völzke
Dokumenttyp:Posterpräsentation
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2019
Organisationseinheit der BAM:3 Gefahrgutumschließungen; Energiespeicher
3 Gefahrgutumschließungen; Energiespeicher / 3.4 Sicherheit von Lagerbehältern
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Angewandte Physik
Freie Schlagwörter:Ageing Management; Cladding Embrittlement; Extended Storage; Ring Compression Test; Spent Nuclear Fuel
Themenfelder/Aktivitätsfelder der BAM:Energie
Energie / Kerntechnische Entsorgung
Veranstaltung:IAEA International Conference on the Management of Spent Fuel from Nuclear Power Reactors
Veranstaltungsort:Vienna, Austria
Beginndatum der Veranstaltung:24.06.2019
Enddatum der Veranstaltung:28.06.2019
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:06.09.2019
Referierte Publikation:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.