Measurement of Elemental Composition of FeNi and SiGe Alloy Thin Films by EMPA and µ-XRF

  • It was demonstrated in the past that the electron probe microanalysis (EPMA) can be applied to determine accurately both elemental composition and thickness of thin films by using the dedicated software package for thin film analysis Stratagem. A relatively small number of film materials such as pure metallic films of platinum and nickel, binary alloys of Fe-Ni, and Pt-Ni-Co ternary alloy films has been reported in literature as working successfully. Further, the software can be applied ‘inversely’, i.e., by feeding it with the thickness of the film and using the determined mass coating, one can easily calculate the film density, which for porous layers leads us to the true film porosity. The present study repeats measurements on an already tested system of Fe-Ni thin films on silicon and reports for the first-time results of analysis on Si-Ge thin films deposited on a non-conductive aluminium oxide substrate. Standard-based and standardless EPMA (with EDS) results were used inIt was demonstrated in the past that the electron probe microanalysis (EPMA) can be applied to determine accurately both elemental composition and thickness of thin films by using the dedicated software package for thin film analysis Stratagem. A relatively small number of film materials such as pure metallic films of platinum and nickel, binary alloys of Fe-Ni, and Pt-Ni-Co ternary alloy films has been reported in literature as working successfully. Further, the software can be applied ‘inversely’, i.e., by feeding it with the thickness of the film and using the determined mass coating, one can easily calculate the film density, which for porous layers leads us to the true film porosity. The present study repeats measurements on an already tested system of Fe-Ni thin films on silicon and reports for the first-time results of analysis on Si-Ge thin films deposited on a non-conductive aluminium oxide substrate. Standard-based and standardless EPMA (with EDS) results were used in combination with Stratagem for the quantification. Further, X-ray fluorescence analysis (XRF) can be used for the determination of elemental composition and thickness of such films as well. In this case, XRF with a μ-focus X-ray source (μ-XRF) attached to a SEM was applied. For quantification, a fundamental parameter (FP) approach has been used to calculate standard-based and standardless results. Compared to EPMA, XRF has a larger information depth and a higher elemental sensitivity because of a generally lower background. Both thin film systems have been chosen as samples of an international round robin test (RRT) organised in the frame of standardisation technical committee ISO/TC 201 ‘Surface chemical analysis’, under the lead of KRISS. The main objective of the RRT is to compare the results of atomic fractions of Fe1-xNix and Si1-xGex alloy films obtained by different surface Analysis techniques, such as X-ray photoelectron spectroscopy (XPS), Auger electron spectroscopy (AES), and secondary ion mass spectrometry (SIMS) applied in the depth-profiling operation mode. Five samples of different atomic fractions of each thin film system, i.e., Fe1-xNix and Si1-xGex, have been grown by ion beam sputter deposition on silicon and Al2O3 wafers, respectively. Reference FeNi and SiGe films with well-known elemental composition and thickness have been also supplied for standard-based analysis. The atomic fractions of all the samples including the references have been certified by RBS (Rutherford backscattering spectrometry) and ICP-AES (inductively coupled plasma atomic emission spectroscopy).zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Poster_Hodoroaba_EMAS2019_KRISS-RRT.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Vasile-Dan HodoroabaORCiD, R. Terborg
Koautor*innen:S. Boehm, K. J. Kim
Dokumenttyp:Posterpräsentation
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2019
Organisationseinheit der BAM:6 Materialchemie
6 Materialchemie / 6.1 Oberflächen- und Dünnschichtanalyse
DDC-Klassifikation:Naturwissenschaften und Mathematik / Chemie / Analytische Chemie
Freie Schlagwörter:EPMA; Fe-Ni; SEM/EDS; Si-Ge; Thin film analysis
Themenfelder/Aktivitätsfelder der BAM:Chemie und Prozesstechnik
Veranstaltung:EMAS 2019 - 16th European Workshop on MODERN DEVELOPMENTS AND APPLICATIONS IN MICROBEAM ANALYSIS
Veranstaltungsort:Trondheim, Norway
Beginndatum der Veranstaltung:19.05.2019
Enddatum der Veranstaltung:23.05.2019
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:29.05.2019
Referierte Publikation:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.