Investigating the microstructure and magnetic properties of La-Fe-Si microwires during fabrication and heat treatment process

  • In this study, the optimized fabrication and evolution of the microstructure and magnetic Transition behavior of the melt-extraction LaFe11.2Si1.8 microwires have been studied. After the optimization of extraction technique (heating power 22 KW, feeding rate 30-50 mm/s, rotation velocity 1700 r/min), the content of La Fe,Si)13 phase in the as-extracted microwires was 54 wt% due to the high solidification velocity, which was increased to 85 wt% via annealing at 1373 K for 20 min. The amount of La(Fe,Si)13 phase was increased and the composition of La(Fe,Si)13 phase became more homogenized through peritectic reaction and short-distance diffusion in the microwires during annealing process. The coexistence of the nanocrystalline and amorphous structures contributed to the broad magnetic Transition temperature range of the as-extracted and annealed microwires. The annealed microwires exhibited a second-order magnetic transformation behavior and showed a maximum magnetic entropy ChangeIn this study, the optimized fabrication and evolution of the microstructure and magnetic Transition behavior of the melt-extraction LaFe11.2Si1.8 microwires have been studied. After the optimization of extraction technique (heating power 22 KW, feeding rate 30-50 mm/s, rotation velocity 1700 r/min), the content of La Fe,Si)13 phase in the as-extracted microwires was 54 wt% due to the high solidification velocity, which was increased to 85 wt% via annealing at 1373 K for 20 min. The amount of La(Fe,Si)13 phase was increased and the composition of La(Fe,Si)13 phase became more homogenized through peritectic reaction and short-distance diffusion in the microwires during annealing process. The coexistence of the nanocrystalline and amorphous structures contributed to the broad magnetic Transition temperature range of the as-extracted and annealed microwires. The annealed microwires exhibited a second-order magnetic transformation behavior and showed a maximum magnetic entropy Change jDSMjmax of 6.2 J/kgK and working temperature interval of 36.0 K under a magnetic field of 20 kOe.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Zhang2019_La-Fe-Si microwire.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:R. Zhang, M. Qian, Anja Waske, H. Shen, X. Zhang
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Journal of Alloys and Compounds
Jahr der Erstveröffentlichung:2019
Organisationseinheit der BAM:8 Zerstörungsfreie Prüfung
8 Zerstörungsfreie Prüfung / 8.0 Abteilungsleitung und andere
Verlag:Elsevier B.V.
Jahrgang/Band:794
Erste Seite:153
Letzte Seite:162
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:La(Fe,Si)13 phase; Magnetocaloric effect; Melt-extraction technique; Peritectic reaction; Short-distance diffusion
Themenfelder/Aktivitätsfelder der BAM:Material
DOI:10.1016/j.jallcom.2019.04.196
ISSN:0925-8388
ISSN:1873-4669
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:29.05.2019
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:03.06.2019
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.