Analysis of moisture transport in unilateral-heated dense high-strength concrete

  • Unilateral thermal exposure of concrete building components induces moisture transport processes that have a significant influence on the spalling behaviour of dense high-strength concrete (HSC). These transport processes are based on evaporation and condensation mechanisms of liquid and gaseous water in the pores as well as the chemically bound water within the concrete. The low permeability of HSC and the formation of a saturated zone within building components (also known as a moisture clog) leads to high water-vapour pressures, which contributes to explosive spalling. The formation of these pressures has already been verified by means of pore-pressure measurement techniques. In addition, the redistribution of the moisture within concrete specimens subject to unilateral thermal exposure has been demonstrated on fractured surfaces. Investigations by means of the nuclear magnetic resonance (NMR) relaxometry technique and neutron radiography have shown one-dimensional changes inUnilateral thermal exposure of concrete building components induces moisture transport processes that have a significant influence on the spalling behaviour of dense high-strength concrete (HSC). These transport processes are based on evaporation and condensation mechanisms of liquid and gaseous water in the pores as well as the chemically bound water within the concrete. The low permeability of HSC and the formation of a saturated zone within building components (also known as a moisture clog) leads to high water-vapour pressures, which contributes to explosive spalling. The formation of these pressures has already been verified by means of pore-pressure measurement techniques. In addition, the redistribution of the moisture within concrete specimens subject to unilateral thermal exposure has been demonstrated on fractured surfaces. Investigations by means of the nuclear magnetic resonance (NMR) relaxometry technique and neutron radiography have shown one-dimensional changes in moisture distribution during thermal exposure. However, none of these methods has been able to depict the moisture distribution in three dimensions (3D), so the link between pore size, concrete micro-structure and moisture content is missing. The research project presented in this paper aims to fill this gap by developing a new multi-level test methodology to characterise non-destructively the temporal course of spatial moisture distribution during unilateral thermal exposure. The procedure used during this programme included the collection of X-ray 3D-computed tomography (CT) measurements using a miniaturised specimen subjected to in-situ thermal exposure and the comparison of those CT results with the results of one-dimensional NMR-relaxometry before and after the heating process. In the first step, a mobile heating device was developed, built and tested. To simulate a unilaterally-heated construction component, a cylindrical specimen made of HSC (Ø = 40 mm, L = 100 mm) was cast into an impermeable glass ceramic shell. The ceramic shell ensured a one-dimensional moisture flux and limited the thermal expansion of the concrete. An additional high-temperature wool (HTW) insulating shell ensured a one-dimensional heat flux. The heating device, which operated using infrared radiation (IR), allowed the unilateral heating of the specimens up to 300 °C using variable heating regimes. In the second step, the mobile heating device was integrated into the CT-scanner, which enabled the collection of measurements before, during and after heating. By subtraction of successive 3D-CT images, X-ray attenuation differences could be resolved three-dimensionally in the specimen and interpreted as changes in the moisture content. Initial results show that this test methodology can monitor the 3D changes of moisture content inside the specimen during thermal exposure. It enables the researcher to visualise areas with moisture accumulation as well as dehydrated areas inside the specimen. Comparative one-dimensional NMR-relaxometry measurements confirm the results of the CT image analysis.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Stelzner_et al_Analysis of moisture transport in unilateral-heated dense high-strength concrete.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Ludwig StelznerORCiD
Koautor*innen:Bartosz Powierza, Frank Weise, Tyler Oesch, R. Dlugosch, Birgit Meng
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2017
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurbau
Freie Schlagwörter:Fire; HPC; HSC; Moisture clog; Moisture transport; NDT; NMR; Spalling; X-ray CT
Veranstaltung:5th International Workshop on Concrete Spalling due to Fire Exposure
Veranstaltungsort:Boras, Sweden
Beginndatum der Veranstaltung:12.10.2017
Enddatum der Veranstaltung:13.10.2017
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.11.2017
Referierte Publikation:Nein
Eingeladener Vortrag:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.