Size effects in miniature specimen creep testing of P91

  • The use of miniaturized specimen geometries in mechanical testing allows extracting the sample material directly from critical components of power plants like e.g. headers and pipes. In this way, both the impacts of the manufacture of the component (including all shaping and tempering influences) and of the complex aging/loading/oxidation conditions during Service can be analyzed and representative mechanical properties are obtained. In the present study, example results of a comparative creep and creep rupture study on P91 tempered martensite ferritic Steel, involving Standard and miniature specimens that were all taken from one batch of material, are presented. Cylindrical creep specimens with a minimum gauge length diameter of 3 mm were used, representing the smallest recommended test geometry of ISO 204. The test results of miniature specimens exhibit all characteristic creep features of tempered martensite ferritic steels, and analysis of the stress and temperature dependence ofThe use of miniaturized specimen geometries in mechanical testing allows extracting the sample material directly from critical components of power plants like e.g. headers and pipes. In this way, both the impacts of the manufacture of the component (including all shaping and tempering influences) and of the complex aging/loading/oxidation conditions during Service can be analyzed and representative mechanical properties are obtained. In the present study, example results of a comparative creep and creep rupture study on P91 tempered martensite ferritic Steel, involving Standard and miniature specimens that were all taken from one batch of material, are presented. Cylindrical creep specimens with a minimum gauge length diameter of 3 mm were used, representing the smallest recommended test geometry of ISO 204. The test results of miniature specimens exhibit all characteristic creep features of tempered martensite ferritic steels, and analysis of the stress and temperature dependence of creep results in values that correspond well to literature data for P91. However, direct comparison with large scale specimen data reveals small but systematic variations in minimum creep rates, elongations at fracture and times to rupture. In our contribution, these differences are discussed in the light of literature findings on specimen size influences in other heat resistant alloys. Size effects need to be considered for a correct interpretation of results from miniature specimen creep tests.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • ECCC2014.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Marck Bismarck, Birgit SkrotzkiORCiD, Jürgen Olbricht
Dokumenttyp:Beitrag zu einem Tagungsband
Veröffentlichungsform:Graue Literatur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):ECCC 2014
Jahr der Erstveröffentlichung:2017
Verlag:Tipography Inail
Verlagsort:Milan
Erste Seite:430
Letzte Seite:435
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Material
Veranstaltung:3rd International ECCC Conference
Veranstaltungsort:Rom, Italy
Beginndatum der Veranstaltung:05.05.2014
Enddatum der Veranstaltung:07.05.2014
ISBN:978-88-7484-510-1
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:07.08.2017
Referierte Publikation:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.