Surface analysis of plasma-deposited polymer films, 1: Time of Flight Static Secondary Ion Mass Spectrometry (ToF-SSIMS) of plasma polystyrene before and after exposure to ambient air

  • Pulsed plasma-deposited polystyrene films were studied by time-of-flight static secondary ion mass spectrometry (ToF-SSIMS) before and after exposure to ambient air. The influence of the external plasma parameters on the secondary ion mass spectra of plasma-deposited polystyrene films was investigated. From these data, information on the chemical character of the plasma polystyrene films was derived. In the range of deposition conditions applied in this study, the fragmentation of styrene is a minor process. The main process is probably the radical chain propagation to polymers. All the polystyrene plasma polymers, relying on ToF-SIMS, seem to be rather similar to a reference polystyrene oligomer sample. When the plasma polymers are exposed to air, extensive oxygen incorporation occurs. Oxygen uptake was found to alter the emission probabilities of secondary ions. A relation between the regularity of the plasma polymers and the amount of oxygen incorporation was found. The result wasPulsed plasma-deposited polystyrene films were studied by time-of-flight static secondary ion mass spectrometry (ToF-SSIMS) before and after exposure to ambient air. The influence of the external plasma parameters on the secondary ion mass spectra of plasma-deposited polystyrene films was investigated. From these data, information on the chemical character of the plasma polystyrene films was derived. In the range of deposition conditions applied in this study, the fragmentation of styrene is a minor process. The main process is probably the radical chain propagation to polymers. All the polystyrene plasma polymers, relying on ToF-SIMS, seem to be rather similar to a reference polystyrene oligomer sample. When the plasma polymers are exposed to air, extensive oxygen incorporation occurs. Oxygen uptake was found to alter the emission probabilities of secondary ions. A relation between the regularity of the plasma polymers and the amount of oxygen incorporation was found. The result was that the chemical regularity of the plasma polystyrene decreases when the effective power in the plasma is increased.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Umut Oran, Sufal Swaraj, Jörg Florian Friedrich, Wolfgang UngerORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Plasma processes and polymers
Jahr der Erstveröffentlichung:2004
Verlag:Wiley-VCH Verl.
Verlagsort:Weinheim
Jahrgang/Band:1
Erste Seite:123
Letzte Seite:133
DOI:10.1002/ppap.200400002
ISSN:1612-8850
ISSN:1612-8869
Verfügbarkeit des Dokuments:Weder Datei noch physisches Exemplar vorhanden ("No Access")
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:24.11.2004
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.