Damage accumulation in short fiber reinforced thermoplast by X-Ray refraction

  • Micro damage structures of fiber reinforced polymers (FRP) can be characterized nondestructively by X-ray refraction topography, which images inner surfaces. The damage accumulation after fatigue treatment of short glass fiber reinforced polybutylene terephthalate (PBT-GF) is correlated to the applied load and the number of cycles. Micro cracks and fiber/matrix debonding during fatigue can be detected separately due to their different direction of X-ray small angle scattering. The residual strength over the crack surface decreases by a linear decay as 30 %, 60 % and 90 % of the materials lifetime is passed.

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Hans-Volker Rudolph, Manfred P. Hentschel, Heinz Ivers
Dokumenttyp:Beitrag zu einem Tagungsband
Veröffentlichungsform:Graue Literatur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Proceedings of the 8th ECNDT
Jahr der Erstveröffentlichung:2002
Herausgeber (Institution):Asociación Española de Ensayos no Destructivos
Verlag:European Federation for Non-Destructive Testing
Verlagsort:Barcelona
Jahrgang/Band:8
Erste Seite:1
Letzte Seite:5
Veranstaltung:8th ECNDT
Veranstaltungsort:Barcelona, Spain
Beginndatum der Veranstaltung:2002-06-17
Enddatum der Veranstaltung:2002-06-21
URL:http://www.ndt.net/article/ecndt02/193/193.htm
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.