Fabrication of porous ceramics made from nano sized alumina powder by gelcasting

  • The gelcasting process was used for manufacturing porous ceramic bodies from nano sized powders. 3 different powders with specific surface areas between 12 and 30 m²/g were used. Solid content of the corresponding slurries was dependent on the milling procedure and the use of a suitable dispersant. For bimodal GradeA powder solid content was as high as 58 vol%. For sintering temperatures between 1250 and 1600°C the porosity varied between 45 and 20%, whereas the pore radii varied between 50 and 91nm. The grain size of crystallites in the sintered microstructures was about 1um. The reflection ratio for visible light increased in comparison to a reference sample made from conventional powder from 0.8 to 0.95 in the wavelenght range around 400nm.

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Gabriele Steinborn, Rolf WäscheORCiD, U. Reichel
Dokumenttyp:Beitrag zu einem Tagungsband
Veröffentlichungsform:Graue Literatur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Proceedings of the 2nd International Conference on Shaping of Advanced Ceramics
Jahr der Erstveröffentlichung:2002
Erste Seite:103
Letzte Seite:108
Veranstaltung:2nd International Conference on Shaping of Advanced Ceramics
Veranstaltungsort:Gent, Belgium
Beginndatum der Veranstaltung:2002-10-24
Enddatum der Veranstaltung:2002-10-26
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.