Fluorinated carbon fibres and their suitability as reinforcement for fluoropolymers

  • The interaction between direct fluorinated carbon fibres and various fluoropolymers (ethylene-chlorotrifluoroethylene, poly vinylidene fluoride, fluorinated ethylene propylene copolymer and tetrafluoroethylene-perfluoro alkoxy vinyl ether copolymer) was studied by means of direct wetting measurements between fibres and the polymer melts and single fibre pull-out tests. The results of both techniques allow the adhesion behaviour between the fibres and the matrices to be predicted. The results obtained show that a low degree of surface fluorination of carbon fibres leads to an improved wettability between the fibres and fluoropolymer melts and this is an indicator for an improved thermodynamic work of adhesion. The apparent interfacial shear strength as measure of practical adhesion, determined by the single fibre pull-out test, increases with increasing degree of surface fluorine content up to a maximum, which depends on the degree of fluorination of the matrix used. The improvedThe interaction between direct fluorinated carbon fibres and various fluoropolymers (ethylene-chlorotrifluoroethylene, poly vinylidene fluoride, fluorinated ethylene propylene copolymer and tetrafluoroethylene-perfluoro alkoxy vinyl ether copolymer) was studied by means of direct wetting measurements between fibres and the polymer melts and single fibre pull-out tests. The results of both techniques allow the adhesion behaviour between the fibres and the matrices to be predicted. The results obtained show that a low degree of surface fluorination of carbon fibres leads to an improved wettability between the fibres and fluoropolymer melts and this is an indicator for an improved thermodynamic work of adhesion. The apparent interfacial shear strength as measure of practical adhesion, determined by the single fibre pull-out test, increases with increasing degree of surface fluorine content up to a maximum, which depends on the degree of fluorination of the matrix used. The improved interaction between the fibre and the matrix is due to an enhanced compatibility at the fibre/matrix interface.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:K.K.C. Ho, Gerhard Kalinka, M.Q. Tran, N.V. Polyakova, A. Bismarck
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Composites science and technology
Jahr der Erstveröffentlichung:2007
Verlag:Elsevier
Verlagsort:Barking
Jahrgang/Band:67
Ausgabe/Heft:13
Erste Seite:2699
Letzte Seite:2706
Freie Schlagwörter:A. Carbon fibres; Adhesion; B. Debonding; B. Interfacial strength
DOI:10.1016/j.compscitech.2007.02.012
ISSN:0266-3538
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:20.09.2007
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.