Effect of Transcrystallization in Carbon Fiber Reinforced Poly(p/phenylene sulfide) Composites on the Interfacial Shear Strength Investigated with the Single Fiber Pull-Out Test
- The effect of transcrystallinity in carbon fiber reinforced poly(p-phenylene sulfide (PPS) composites on the apparent shear strength was investigated with the single fiber pull-out test. Transcrystalline zones around the reinforcing fibers do not seem to improve the adhesion level significantly. Neighbor fibers hinder the formation of the transcrystalline zone and a ductile fracture behavior can be observed. However, the apparent strength level is slightly higher for composites containing such reinforcing neighbor fibers compared with single fiber composite samples. During annealing a brittle interface can be formed in the multifiber composite yielding a higher level of the apparent shear strength.
Autor*innen: | Eckhard Schulz, Gerhard Kalinka, W. Auersch |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Journal of macromolecular science B |
Jahr der Erstveröffentlichung: | 1996 |
Verlag: | Dekker Chemistry |
Verlagsort: | New York, NY |
Jahrgang/Band: | 35 |
Ausgabe/Heft: | 3-4 |
Erste Seite: | 527 |
Letzte Seite: | 546 |
Freie Schlagwörter: | Adhäsion; Haftung; Interface; Kristallisation; Pull-out; Reibung; Thermoplaste; Transkristallisation; Verbundwerkstoffe |
DOI: | 10.1080/00222349608220393 |
ISSN: | 0022-2348 |
ISSN: | 1525-609X |
Verfügbarkeit des Dokuments: | Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access") |
Bibliotheksstandort: | Sonderstandort: Publica-Schrank |
Datum der Freischaltung: | 19.02.2016 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 30.01.2006 |