Flammability of layered silicate epoxy nanocomposites combined with low-melting inorganic ceepree glass

  • Tetraphenylphosphonium modified layered silicate epoxy nanocomposite (EP/TPPMMT) combined with low-melting silicate glass, Ceepree (CP) is investigated by thermal analysis, flammability tests and cone calorimeter at different heat fluxes. Adding CP and TPPMMT does not change the pyrolysis apart from increasing inorganic residue. The total heat evolved (THE) is changed insignificantly, as neither relevant additional carbonaceous charring nor flame inhibition occurs. However, flame retardancy is clearly observed due to an inorganic-carbonaceous surface protection layer. The peak heat released rate (PHRR) is reduced by around 32–42% when 5 wt% TPPMMT is added, and 51–63% when 10 wt% CP is added. PHRR reduction less than expected is observed when both additives are combined. The reduction is greater than that achieved by using TPPMMT but less than when only CP is used. The morphology of fire residue is investigated by scanning electron microscope on different length scales and turns out toTetraphenylphosphonium modified layered silicate epoxy nanocomposite (EP/TPPMMT) combined with low-melting silicate glass, Ceepree (CP) is investigated by thermal analysis, flammability tests and cone calorimeter at different heat fluxes. Adding CP and TPPMMT does not change the pyrolysis apart from increasing inorganic residue. The total heat evolved (THE) is changed insignificantly, as neither relevant additional carbonaceous charring nor flame inhibition occurs. However, flame retardancy is clearly observed due to an inorganic-carbonaceous surface protection layer. The peak heat released rate (PHRR) is reduced by around 32–42% when 5 wt% TPPMMT is added, and 51–63% when 10 wt% CP is added. PHRR reduction less than expected is observed when both additives are combined. The reduction is greater than that achieved by using TPPMMT but less than when only CP is used. The morphology of fire residue is investigated by scanning electron microscope on different length scales and turns out to be the key to understanding the efficiency of flame retardancy. The fire residue of EP/CP shows a layered structure, whereas separated columns limit the barrier properties for EP/5%TPPMMT on the micrometer scale. Columns dominating the fire residue structure of EP/5%TPPMMT/10%CP deteriorate the fire retardancy, whereas a more integral structure at the top of the residue causes the improvement over EP/5%TPPMMT. POLYM. ENG. SCI., 2012. © 2011 Society of Plastics Engineerszeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Guang Mei Wu, Bernhard SchartelORCiD, M. Kleemeier, A. Hartwig
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Polymer engineering & science
Jahr der Erstveröffentlichung:2012
Herausgeber (Institution):Society of Plastics Engineers
Verlag:Wiley
Verlagsort:Hoboken, NY
Jahrgang/Band:52
Ausgabe/Heft:3
Erste Seite:507
Letzte Seite:517
Freie Schlagwörter:Ceepree; Epoxy resin; Flame retardancy; Low melting glasses; Nanocomposites
DOI:10.1002/pen.22111
ISSN:0032-3888
ISSN:1548-2634
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:12.03.2012
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.