Creep damage of single-crystal nickel base superalloys: mechanisms and effect on low cycle fatigue
- The main mechanisms of creep damage of single-crystal nickel-base superalloys are the loss of the interface coherency, coarsening of the γ / γ'-microstructure, precipitation of topologically closed packed phases and growth of porosity. This degradation deteriorates the mechanical properties such as yield stress, creep lifetime and especially low-cycle fatigue life, which can be reduced nearly by a factor of 10. The degradation kinetics during creep was characterised quantitatively on the superalloy CMSX-4. A new non-destructive testing technique was applied to cover a wide test parameter range with few specimens in a relatively short time: repeated load annealing of wedge shaped specimens.
Autor*innen: | Alexander Epishin, T. Link, Hellmuth Klingelhöffer, Bernard FedelichORCiD, Pedro Dolabella PortellaORCiD |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Materials at high temperatures |
Jahr der Erstveröffentlichung: | 2010 |
Verlag: | Science Reviews |
Verlagsort: | St. Albans, Herts. [u.a.] |
Jahrgang/Band: | 27 |
Ausgabe/Heft: | 1 |
Erste Seite: | 53 |
Letzte Seite: | 59 |
Freie Schlagwörter: | Creep damage; Low-cycle fatigue; Nickel-base superalloys; Porosity; Prior exposure; Rafting |
DOI: | 10.3184/096034009X12603595726283 |
ISSN: | 0960-3409 |
Verfügbarkeit des Dokuments: | Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access") |
Bibliotheksstandort: | Sonderstandort: Publica-Schrank |
Datum der Freischaltung: | 19.02.2016 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 27.06.2011 |