Artificial plastic aging as a framework for microplastics ecotoxicity evaluation
- Microplastics are widely distributed in aquatic and terrestrial environments, up to now less is known on toxicological impacts under realistic conditions. Research so far has focused mainly on the impacts on organisms by fresh plastic fragments or beats. However, plastic materials found in the environment are mainly a mixture of different polymers and additives and particularly degraded during aging processes. Although especially oxidized degradation products might escape from plastic materials during aging, there is a lack of information on potentially adverse effects on aquatic biota. The latter is of particular interest as oxidized chemicals become more water soluble due to higher polarity and are more bio-available, therefore. The present study focused on plastic leachates of polystyrene (PS) and polylactic acid (PLA), which were derived from alternating stress by hydrolysis and UV radiation. Test specimen of PS, PLA or PS/PLA blends (each 50 %) were alternatingly maintained inMicroplastics are widely distributed in aquatic and terrestrial environments, up to now less is known on toxicological impacts under realistic conditions. Research so far has focused mainly on the impacts on organisms by fresh plastic fragments or beats. However, plastic materials found in the environment are mainly a mixture of different polymers and additives and particularly degraded during aging processes. Although especially oxidized degradation products might escape from plastic materials during aging, there is a lack of information on potentially adverse effects on aquatic biota. The latter is of particular interest as oxidized chemicals become more water soluble due to higher polarity and are more bio-available, therefore. The present study focused on plastic leachates of polystyrene (PS) and polylactic acid (PLA), which were derived from alternating stress by hydrolysis and UV radiation. Test specimen of PS, PLA or PS/PLA blends (each 50 %) were alternatingly maintained in water at 45 °C for five days and UV radiated at 45 °C for two days, for in total six weeks. Ecotoxicological effects of potentially generated degradation products of plastic materials in the storage water (mineral water, pH: 7.2) were detected by algae growth inhibition tests with Desmodesmus suspicatus and photosystem II inhibition tests with Raphidocelis subcapitata. Results clearly indicate inhibitory effects on algae growth by contaminants in the storage water of stressed plastic materials with increasing growth inhibition of proceeding hydrolysis and UV stress times. Here, different plastics cause variable responses of algal growth. First chemical analyses indicate dissolved monomers and their oxidation products of plastic materials as possible driver of detected ecotoxicological effects, since detected microplastic particles do not seem to harm algae. The existing data highlight the relevance of plastic aging as a framework for microplastic ecotoxicity evaluation and allow a proof of concept.…
Autor*innen: | M. Lukas |
---|---|
Koautor*innen: | Maria Kittner, Korinna Altmann, T. Kremer, R. Kochmann, L. Isernhinke, U. Braun |
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2022 |
Organisationseinheit der BAM: | 6 Materialchemie |
6 Materialchemie / 6.6 Physik und chemische Analytik der Polymere | |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Sanitär- und Kommunaltechnik; Umwelttechnik |
Freie Schlagwörter: | Ecotoxicity; Microplastic |
Themenfelder/Aktivitätsfelder der BAM: | Umwelt |
Veranstaltung: | 37. DGL-Tagung, Universität Konstanz |
Veranstaltungsort: | Konstanz, Germany |
Beginndatum der Veranstaltung: | 19.09.2022 |
Enddatum der Veranstaltung: | 23.09.2022 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 04.10.2022 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |