Investigation on the microstructure of ultra high performance concrete

  • Ultra-high performance concrete (UHPC) is characterised by compressive strengths above 150 MPa and an outstanding durability. These properties are achieved by optimisation of the mixture composition, the mixing procedure as well as the curing conditions of the concrete. Heat curing as well as the use of vacuum mixers may contribute to the high strength. The very high brittleness of UHPC can be compensated by the addition of steel or polymer fibres. UHPC is produced using a very low water/cement ratio of 0.25 or smaller in combination with adding of polycarboxylate ether based superplasticisers. Furthermore, finest cements with contents of 500 kg/m³, defined selections of coarse and fine aggregates with a maximum grain size between 0.5 and 8 mm and fine pozzolanic (silica fume, fly ash) and inert additives (quartz filler) are used. In doing so, the aim is to obtain a very high packing density of the cement paste matrix and the aggregate/paste interface while a very homogeneousUltra-high performance concrete (UHPC) is characterised by compressive strengths above 150 MPa and an outstanding durability. These properties are achieved by optimisation of the mixture composition, the mixing procedure as well as the curing conditions of the concrete. Heat curing as well as the use of vacuum mixers may contribute to the high strength. The very high brittleness of UHPC can be compensated by the addition of steel or polymer fibres. UHPC is produced using a very low water/cement ratio of 0.25 or smaller in combination with adding of polycarboxylate ether based superplasticisers. Furthermore, finest cements with contents of 500 kg/m³, defined selections of coarse and fine aggregates with a maximum grain size between 0.5 and 8 mm and fine pozzolanic (silica fume, fly ash) and inert additives (quartz filler) are used. In doing so, the aim is to obtain a very high packing density of the cement paste matrix and the aggregate/paste interface while a very homogeneous microstructure with a high calcium silicate hydrate (CSH) portion is formed. In the case of optimal mixing and curing conditions, UHPC contains almost no pores and microcracks. Therefore, studies of porosity and pore structure are very important to characterise UHPC materials in connection with the mixture optimisation. Here, the experimental results for UHPC are presented in comparison with those of high-strength concrete (100 MPa) and normal-strength concrete (35 MPa), respectively.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Investigation on the microstructure of ultra high performance concrete.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Peter Klobes
Koautor*innen:Katrin Rübner, Carsten Prinz, S. Hempel
Dokumenttyp:Posterpräsentation
Veröffentlichungsform:Präsentation
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):8th International Symposium on the characterisation of Porous Solids
Jahr der Erstveröffentlichung:2008
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Veranstaltung:8th International Symposium on the characterisation of Porous Solids
Veranstaltungsort:Edinburgh, Scotland
Beginndatum der Veranstaltung:11.06.2008
Enddatum der Veranstaltung:14.06.2008
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:19.02.2016
Referierte Publikation:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.