Formation of Creep Damage of 316L Produced by Laser Powder Bed Fusion
- The damage mechanisms of metallic components produced by process laser powder bed fusion differ significantly from those typically observed in conventionally manufactured variants of the same alloy. This is due to the unique microstructures of additively manufactured materials. Herein, the focus is on the study of the evolution of creep damage in stainless steel 316L specimens produced by laser powder bed fusion. X-ray computed tomography is used to unravel the influence of the process-specific microstructure from the influence of the initial void distribution on creep damage mechanisms. The void distribution of two specimens tested at 600 °C and 650 °C is analyzed before a creep test, after an interruption, and after fracture. The results indicate that the formation of damage is not connected to the initial void distribution. Instead, damage accumulation at grain boundaries resulting from intergranular cracking is observed.
Autor*innen: | Alexander UlbrichtORCiD |
---|---|
Koautor*innen: | Luis Alexander Ávila Calderón, Konstantin Sommer, Gunther MohrORCiD, Alexander Evans, Birgit Skrotzki, Giovanni Bruno |
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2024 |
Organisationseinheit der BAM: | 5 Werkstofftechnik |
5 Werkstofftechnik / 5.1 Mikrostruktur Design und Degradation | |
5 Werkstofftechnik / 5.2 Metallische Hochtemperaturwerkstoffe | |
8 Zerstörungsfreie Prüfung | |
8 Zerstörungsfreie Prüfung / 8.5 Röntgenbildgebung | |
9 Komponentensicherheit | |
9 Komponentensicherheit / 9.6 Additive Fertigung metallischer Komponenten | |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | AISI 316L; Additive Manufacturing; Computed Tomography; Creep; Laser Powder Bed Fusion; Microstructure; PBF-LB/M/316L |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Additive Fertigung | |
Material / Degradation von Werkstoffen | |
Veranstaltung: | 4th Symposium on Materials and Additive Manufacturing - Additive 2024 |
Veranstaltungsort: | Berlin, Germany |
Beginndatum der Veranstaltung: | 12.06.2024 |
Enddatum der Veranstaltung: | 14.06.2024 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 18.06.2024 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |