Influence of manufacturing conditions on the cracking susceptibility of AHSS during resistance spot welding

  • The influence of two different weld imperfections (gap/crack) on the fatigue behaviour of spot welded joints was tested Surface cracks have no influence on the fatigue life Samples with cracks in the electrode indentation /HAZ where tested Stiffness curves are not significantly influenced by surface cracks 3D FE-Simulation demonstrate no changes of stress due to surface imperfections • Welding under external forces was found suitable for characterizing AHSS materials New quick and easy-to-perform procedure for establishing a material ranking regarding cracking susceptibility

Volltext Dateien herunterladen

  • 20161004_Technical Paper_Rethmeier SMWC16.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Michael RethmeierORCiD
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2016
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:3D-FE-Simulation
Veranstaltung:AWS Sheet Metal Welding Conference XVII
Veranstaltungsort:Livonia, MI, USA
Beginndatum der Veranstaltung:19.10.2016
Enddatum der Veranstaltung:20.10.2016
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:21.11.2016
Referierte Publikation:Nein
Eingeladener Vortrag:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.