Structure−property relationships of hyperbranched polyamine ester/Ka-DCA nanocomposites
- Hyperbranched polyamine ester (HPAE)/ kaolinite nanocomposites were papered via an ex situ (solution-based) method. The kaolinite has been modified by dodecylamine (DCA). SAXS measurements revealed that the Ka interlayer space increased from 0.71 to 3.6 nm-1. A partly exfoliated structure of the HPA/Ka-DCA nanocomposites was proved by SAXS and TEM. By a combination of BDS and SHS, the relaxation properties of the nanocomposites were investigated in dependence on frequency and temperature. The activation energies of γ-relaxation for the nanocomposites were lower than the values found for the pure HPAE. The segmental dynamics (α- relaxation) was found to be screened out by the conductivity contribution. While it is retrieved by SHS employing AC-chip calorimetry. A systematic change of the dynamic glass transition estimated by AC-chip calorimetry was observed, which is in agreement with a behavior expected for a confined sample. The confinement effect of the Ka-DCA nanofillers reducesHyperbranched polyamine ester (HPAE)/ kaolinite nanocomposites were papered via an ex situ (solution-based) method. The kaolinite has been modified by dodecylamine (DCA). SAXS measurements revealed that the Ka interlayer space increased from 0.71 to 3.6 nm-1. A partly exfoliated structure of the HPA/Ka-DCA nanocomposites was proved by SAXS and TEM. By a combination of BDS and SHS, the relaxation properties of the nanocomposites were investigated in dependence on frequency and temperature. The activation energies of γ-relaxation for the nanocomposites were lower than the values found for the pure HPAE. The segmental dynamics (α- relaxation) was found to be screened out by the conductivity contribution. While it is retrieved by SHS employing AC-chip calorimetry. A systematic change of the dynamic glass transition estimated by AC-chip calorimetry was observed, which is in agreement with a behavior expected for a confined sample. The confinement effect of the Ka-DCA nanofillers reduces the glass transition temperature Tg and enhances, meanwhile, the electrical conductivity of the polymer. By comparing the temperature dependence of the dynamic glass transition measured with SHS and that of the dc conductivity measured by dielectric spectroscopy, a decoupling in their temperature dependencies was found. With increasing concentration of the nanofiller, which results in a stronger glass-formation behavior, this decoupling becomes weaker.…
Autor*innen: | Shereen Omara |
---|---|
Weitere Person: | Mona Rehim, Gamal Turky, Sherif Madkour, Andreas SchönhalsORCiD |
Dokumenttyp: | Posterpräsentation |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2018 |
Organisationseinheit der BAM: | 6 Materialchemie |
6 Materialchemie / 6.6 Physik und chemische Analytik der Polymere | |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Nanocomposites |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Veranstaltung: | Spring Meeting of German Physical Society |
Veranstaltungsort: | Berlin, Germany |
Beginndatum der Veranstaltung: | 12.03.2018 |
Enddatum der Veranstaltung: | 16.03.2918 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 20.03.2018 |
Referierte Publikation: | Nein |