Fatigue limit estimation of welded joints under constant amplitude uniaxial loading adopting the cyclic R-curve analysis

  • Most of the in-service failures of welded structures are due to fatigue damage occurring in the joints. Damage tolerant approaches based on the principles of Fracture Mechanics have been shown to play a key role in this framework, as the fatigue limit is defined by the non-propagating condition of multiple defects at the weld toe. The fatigue limit assessment can be performed using the cyclic R-curve analysis which consists in comparing the driving force of a crack propagating into a component, which depends on the geometry, material and external loads, with its resistance curve, i.e. the cyclic R-curve. The crack propagation occurs whenever the crack driving force is higher than the resistance to fatigue crack propagation, while the crack is arrested in the opposite case. Consequently, this suggests that the fatigue limit of a component is defined as that stress level at which the crack driving force curve is tangent to the crack resistance curve. In the present work, the cyclicMost of the in-service failures of welded structures are due to fatigue damage occurring in the joints. Damage tolerant approaches based on the principles of Fracture Mechanics have been shown to play a key role in this framework, as the fatigue limit is defined by the non-propagating condition of multiple defects at the weld toe. The fatigue limit assessment can be performed using the cyclic R-curve analysis which consists in comparing the driving force of a crack propagating into a component, which depends on the geometry, material and external loads, with its resistance curve, i.e. the cyclic R-curve. The crack propagation occurs whenever the crack driving force is higher than the resistance to fatigue crack propagation, while the crack is arrested in the opposite case. Consequently, this suggests that the fatigue limit of a component is defined as that stress level at which the crack driving force curve is tangent to the crack resistance curve. In the present work, the cyclic R-curve analysis has been adopted for determining the fatigue limit of stress-relieved transverse non-load-carrying joints made of S355 structural steel and subjected to fatigue axial loadings. Experimental tests have been performed to evaluate the fatigue limit of the joints. The driving force, identified by the applied Stress Intensity Factor (SIF), has been evaluated by means of linear elastic finite element analysis taking advantage of the Peak Stress Method for its rapid estimation. Based on the experimental observations that the crack initiation and early crack growth phases in welded joints occur within the Heat Affected Zone (HAZ) the cyclic R-curve has been experimentally derived for both the base metal and HAZ material.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Ppt_ECF23_Fatigue Limit_VecMenModMad_rev00.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Luca Vecchiato
Koautor*innen:Giovanni Meneghetti, Giovanni Moda, Mauro Madia
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2022
Organisationseinheit der BAM:9 Komponentensicherheit
9 Komponentensicherheit / 9.4 Integrität von Schweißverbindungen
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Cyclic R-curve; Fatigue Limit; Welded Joints
Themenfelder/Aktivitätsfelder der BAM:Material
Material / Degradation von Werkstoffen
Veranstaltung:European Conference on Fracture 2022 (ECF23)
Veranstaltungsort:Funchal, Portugal
Beginndatum der Veranstaltung:27.06.2022
Enddatum der Veranstaltung:01.07.2022
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:13.07.2022
Referierte Publikation:Nein
Eingeladener Vortrag:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.