Fatigue behavior of self-healing glass fiber/epoxy composites with addition of poly (ethylene-co-methacrylic acid) (EMAA)
- The interest in repair technologies for polymer composites has increased significantly over the last decades, due to the growing use of these materials in structural applications. In this study, poly (ethylene-co-methacrylic acid) (EMAA) was used as self-healing agent to glass fiber/epoxy composite. Materials with EMAA contents of 2 wt% and 5 wt% were manufactured using Resin Transfer Molding (RTM) and the effects of the healing agent on the properties were investigated using tensile tests and Dynamic Mechanical Analysis (DMA). Results show slight variation of properties, which was more pronounced as the content of EMAA increased. In addition, the healing efficiency was investigated through fatigue tests and the addition of higher content of EMAA increased the number of cycles to failure after the healing activation cycle.
Autor*innen: | A. Azevedo do Nascimento, Volker TrappeORCiD, J. D. Diniz Melo, A. P. Cysne Barbosa |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Polymer Testing |
Jahr der Erstveröffentlichung: | 2022 |
Organisationseinheit der BAM: | 5 Werkstofftechnik |
5 Werkstofftechnik / 5.3 Polymere Verbundwerkstoffe | |
Veröffentlichende Institution: | Bundesanstalt für Materialforschung und -prüfung (BAM) |
Verlag: | Elsevier Ltd. |
Jahrgang/Band: | 117 |
Aufsatznummer: | 107863 |
Erste Seite: | 1 |
Letzte Seite: | 10 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Fatigue; Glass fiber-epoxy composites; Self-healing; Smart materials |
Themenfelder/Aktivitätsfelder der BAM: | Material |
DOI: | 10.1016/j.polymertesting.2022.107863 |
URN: | urn:nbn:de:kobv:b43-569661 |
ISSN: | 0142-9418 |
Verfügbarkeit des Dokuments: | Datei für die Öffentlichkeit verfügbar ("Open Access") |
Lizenz (Deutsch): | Creative Commons - CC BY-NC-ND - Namensnennung - Nicht kommerziell - Keine Bearbeitungen 4.0 International |
Datum der Freischaltung: | 08.02.2023 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 26.02.2024 |
Schriftenreihen ohne Nummerierung: | Wissenschaftliche Artikel der BAM |