Detection and understanding of the chunky graphite degeneration in ferritic spheroidal graphite cast iron materials with respect to fatigue
- CHG is very different compared to other graphite degenerations or defects; Filigree, multi-branched string-like, 3d interconnected structure; Morphology and volumetric amount of CHG cannot be accessed by stereological interpretation of 2d section data; Field-tested, technically established method to quantify CHG in components not available; Fatigue: CHG causes substantial reduction in fatigue limit and significant increase in crack growth rate; Therefore: Avoid or exclude CHG!
Autor*innen: | Wolfram BaerORCiD |
---|---|
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2020 |
Organisationseinheit der BAM: | 9 Komponentensicherheit |
9 Komponentensicherheit / 9.6 Additive Fertigung metallischer Komponenten | |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Chunky graphite degeneration; Correlation microstructure to properties; Ductile cast iron; Fatigue |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Degradation von Werkstoffen | |
Veranstaltung: | 4th International Symposium on Fatigue Design and Material Defects |
Veranstaltungsort: | Online meeting |
Beginndatum der Veranstaltung: | 26.05.2020 |
Enddatum der Veranstaltung: | 28.05.2020 |
Verfügbarkeit des Dokuments: | Weder Datei noch physisches Exemplar vorhanden ("No Access") |
Datum der Freischaltung: | 01.03.2022 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |