Defects as a root cause for fatigue failure of metallic components
- The Topic of the presentationis a discussion on defects which can cause failure in cyclically loaded metallic components. Although also touching Features such as material defects such as pores or micro-shrinkages, etc. and geometric defects such as surface roughness and secondary notches (which are not considered in the design process) which origin in manufacturing, and others the presentation concentrates on non-metallic inclusions. It is prefaced by an introduction to the life cycle of a fatigue crack from initiation up to fracture. Special emphasis is put on the fact that only cracks which are not arrested during one of their distinct Propagation stages can grow to a critical size.
Autor*innen: | Uwe Zerbst |
---|---|
Koautor*innen: | Christian Klinger, Dirk BettgeORCiD |
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2018 |
Organisationseinheit der BAM: | 5 Werkstofftechnik |
5 Werkstofftechnik / 5.1 Mikrostruktur Design und Degradation | |
9 Komponentensicherheit | |
9 Komponentensicherheit / 9.0 Abteilungsleitung und andere | |
9 Komponentensicherheit / 9.4 Integrität von Schweißverbindungen | |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Material defects; Metallic components; Micro-shrinkages |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Veranstaltung: | VIII. International Conference on Engineering Failure Analysis |
Veranstaltungsort: | Budapest, Ungarn |
Beginndatum der Veranstaltung: | 08.06.2018 |
Enddatum der Veranstaltung: | 11.06.2018 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 06.12.2018 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |