Full notch creep test (FNCT) of PE-HD – Characterization and differentiation of brittle and ductile fracture behavior during environmental stress cracking (ESC)
- The damage mechanisms slow crack growth (SCG) and environmental stress cracking (ESC), relevant for PE-HD materials are characterized based on improved full notch creep testing (FNCT) of two selected typical PE-HD materials for container applications. In this context, a distinction of the failure mechanisms as well as a categorization of involved media is suggested. Employing a novel FNCT device, elongation data were obtained in addition to conventional time-to-failure results of stress-dependent as well as temperature-dependent measurements. Changes in failure behavior, as determined by fracture surface analysis based on light microscopy (LM) and laser scanning microscopy (LSM), are correlated with FNCT results and used to introduce an additional possibility for the identification of brittle/ductile fracture behavior.
Autor*innen: | Markus SchillingORCiD, Ute Niebergall, Martin BöhningORCiD |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Polymer Testing |
Jahr der Erstveröffentlichung: | 2017 |
Verlag: | Elsevier |
Verlagsort: | Amsterdam |
Jahrgang/Band: | 64 |
Erste Seite: | 156 |
Letzte Seite: | 166 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurbau | |
Freie Schlagwörter: | Environmental stress cracking (ESC); Full notch creep test (FNCT); High-density polyethylene (PE-HD); Slow crack growth (SCG) |
DOI: | 10.1016/j.polymertesting.2017.09.043 |
ISSN: | 0142-9418 |
ISSN: | 1873-2348 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 12.10.2017 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 04.01.2018 |