LIBS In situ Chemical Analysis in Duplex Stainless Steel Welding
- The high corrosion resistance and good mechanical properties of duplex stainless steel (DSS) are due to its special chemical composition, which is a balanced phase ratio of ferrite (α) and austenite (γ). Many industrial applications require the integration of DSS components. For this, tungsten inert gas welding (TIG) is an excellent choice, as it allows an automated operation with high reproducibility. However, when the weld pool solidifies, critical ratios of α- and γ- phases can occur, which leads to solidification cracking, increased susceptibility to corrosion, and a decrease in ductility and critical strength. Previous studies have shown that these defects can be caused by the accumulation of manganese and chromium in the heat affected zone (HAZ), and this accumulation can be detected using LIBS.
Unlike conventional LIBS analyses, which requires reference samples to generate a calibration curve, calibration-free LIBS (CF-LIBS) can determine the chemical composition solely fromThe high corrosion resistance and good mechanical properties of duplex stainless steel (DSS) are due to its special chemical composition, which is a balanced phase ratio of ferrite (α) and austenite (γ). Many industrial applications require the integration of DSS components. For this, tungsten inert gas welding (TIG) is an excellent choice, as it allows an automated operation with high reproducibility. However, when the weld pool solidifies, critical ratios of α- and γ- phases can occur, which leads to solidification cracking, increased susceptibility to corrosion, and a decrease in ductility and critical strength. Previous studies have shown that these defects can be caused by the accumulation of manganese and chromium in the heat affected zone (HAZ), and this accumulation can be detected using LIBS.
Unlike conventional LIBS analyses, which requires reference samples to generate a calibration curve, calibration-free LIBS (CF-LIBS) can determine the chemical composition solely from the emission spectrum of the plasma. Numerous publications show that CF-LIBS is a fast and efficient analytical method for quantitative analysis of metal samples.
We present the results of in situ CF-LIBS analysis during TIG DSS welding. Using a new approach, it is possible to quantitatively determine the chemical composition of the weld metal directly in the welding process. The results of the CF-LIBS analysis are compared with the results of the calibration-based PLS analysis and reasonable agreement is found. Thus, the CF-LIBS method offers the significant advantage of quickly measuring in situ the concentrations of the main alloying elements that prevent the formation of welding defects, without the tedious calibration procedure.…
Autor*innen: | Lukas QuackatzORCiD |
---|---|
Weitere Person: | Igor B. GornushkinORCiD, Axel Griesche, Thomas KannengießerORCiD, Kai Treutler, Volker Wesling |
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2023 |
Organisationseinheit der BAM: | 9 Komponentensicherheit |
9 Komponentensicherheit / 9.4 Integrität von Schweißverbindungen | |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Calibration free; Duplex stainless steel; In situ measurement; LIBS; TIG welding |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Degradation von Werkstoffen | |
Veranstaltung: | EMSLIBS 2023 |
Veranstaltungsort: | Porto, Portugal |
Beginndatum der Veranstaltung: | 04.09.2023 |
Enddatum der Veranstaltung: | 07.09.2023 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 19.09.2023 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |