Nanosecond laser damage of optical multimode fibers
- For pulse laser materials processing often optical step index and gradient index multimode fibers with core diameters ranging from 100 to 600 μm are used. The design of a high power fiber transmission system must take into account limitations resulting from both surface and volume damage effects. Especially, breakdown at the fiber end faces and self-focusing in the fiber volume critically influence the fiber performance. At least operation charts are desirable to select the appropriate fiber type for given laser parameters. In industry-relevant studies the influence of fiber core diameter and end face preparation on laser-induced (surface) damage thresholds (LIDT) was investigated for frequently used all-silica fiber types (manufacturer LEONI). Experiments on preform material (initial fiber material) and compact specimens (models of the cladding and coating material) accompanied the tests performed in accordance with the relevant LIDT standards ISO 11254-1 and ISO 11254-2 for 1-on-1For pulse laser materials processing often optical step index and gradient index multimode fibers with core diameters ranging from 100 to 600 μm are used. The design of a high power fiber transmission system must take into account limitations resulting from both surface and volume damage effects. Especially, breakdown at the fiber end faces and self-focusing in the fiber volume critically influence the fiber performance. At least operation charts are desirable to select the appropriate fiber type for given laser parameters. In industry-relevant studies the influence of fiber core diameter and end face preparation on laser-induced (surface) damage thresholds (LIDT) was investigated for frequently used all-silica fiber types (manufacturer LEONI). Experiments on preform material (initial fiber material) and compact specimens (models of the cladding and coating material) accompanied the tests performed in accordance with the relevant LIDT standards ISO 11254-1 and ISO 11254-2 for 1-on-1 and S-on-1 illumination conditions, respectively. The relation beam diameter vs. LIDT was investigated for fused silica fibers and preforms. Additionally, the laser-induced (bulk) damage threshold of fused silica preform material F300 (manufacturer Heraeus) in dependence on external mechanical stress simulating fiber bending was measured. All experiments were performed with 10-ns laser pulses at 1064 and 532 nm wavelength with a Gaussian beam profile.…
Autor*innen: | Jörg KrügerORCiD |
---|---|
Koautor*innen: | Guido Mann |
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2016 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Nanosecond Pulses; Nd:YAG laser; Optical multimode fiber Laser induced damage |
Veranstaltung: | Pacific Rim Laser Damage Conference |
Veranstaltungsort: | Yokohama, Japan |
Beginndatum der Veranstaltung: | 18.05.2016 |
Enddatum der Veranstaltung: | 20.05.2016 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 27.05.2016 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |