Influence of casting skin on fatigue lifetime of ferritic ductile cast iron
- The fatigue behaviour of cast iron is usually investigated on machined specimens. Components of cast iron, however, have a casting skin; therefore the investigation of the influence of the casting skin on the lifetime is of interest. To study this influence isothermal fatigue tests were carried out on heat-resisting spheroidal graphite cast iron EN GJS SiMo 4.05 in 4–point-bending set-up at 400 °C. Specimens with and without casting skin were investigated comparatively. The number of cycles to failure was significantly lower for specimens with casting skin. Metallographic investigations underline the reduction of lifetime caused by casting skin.
Autor*innen: | Birgit RehmerORCiD, Birgit SkrotzkiORCiD, Steffen Glaubitz |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Materials Testing |
Jahr der Erstveröffentlichung: | 2017 |
Verlag: | Carl Hanser Verlag |
Verlagsort: | München |
Jahrgang/Band: | 59 |
Ausgabe/Heft: | 1 |
Erste Seite: | 5 |
Letzte Seite: | 10 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Cast iron; Casting skin; Fatigue; Lifetime |
ISSN: | 0025-5300 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 10.01.2017 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 23.03.2017 |