Depth dependent phase identification of corrosion zones in ferritic alloys by micro-X-ray absorption near edge structure spectroscopy
- Ferritic steels with chromium contents up to 13 wt% are used as materials for power plant components as boiler materials (< 2 wt% Cr) and super heater tubes (> 9 wt% Cr). These materials are subject to aggressive corrosion caused by hot gases such as CO2, H2O, O2 and SO2. Especially SO2 causes fatal corrosion even as a minor component. To examine sulfurous corrosion mechanisms, experiments with pure SO2 were conducted. A proper analysis of the material changes requires phase identification and quantification with a high lateral resolution within the corrosion scale.
Autor*innen: | Kathrin Nützmann |
---|---|
Koautor*innen: | Ana de Oliveira Guilherme BuzanichORCiD, Martin RadtkeORCiD, Uwe Reinholz, Christiane Stephan-ScherbORCiD, Franziska EmmerlingORCiD |
Dokumenttyp: | Posterpräsentation |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2017 |
DDC-Klassifikation: | Naturwissenschaften und Mathematik / Chemie / Analytische Chemie |
Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten | |
Freie Schlagwörter: | Corosion; Steel; XANES |
Veranstaltung: | ANAKON2017 |
Veranstaltungsort: | Tübingen, Germany |
Beginndatum der Veranstaltung: | 03.04.2017 |
Enddatum der Veranstaltung: | 06.04.2017 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 30.05.2017 |
Referierte Publikation: | Nein |