Age-hardening behaviour, microstructure and corrosion resistance of the copper alloyed stainless steel 1.4542
- The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion re-sistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in allThe copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion re-sistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hardening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion re-sistance due to chromium depletion.…
Autor*innen: | N. Kauss, Paul Rosemann, T. Halle |
---|---|
Dokumenttyp: | Posterpräsentation |
Veröffentlichungsform: | Präsentation |
Sprache: | Deutsch |
Jahr der Erstveröffentlichung: | 2018 |
Organisationseinheit der BAM: | 7 Bauwerkssicherheit |
7 Bauwerkssicherheit / 7.6 Korrosion und Korrosionsschutz | |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Corrosion; Corrosion resistance; Corrosion testing; EPR; Heat treatment; Martensitic stainless steels; REM; Stainless steel; ThermoCalc |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Degradation von Werkstoffen | |
Veranstaltung: | EUROCORR 2018 |
Veranstaltungsort: | Krakow, Poland |
Beginndatum der Veranstaltung: | 09.09.2018 |
Enddatum der Veranstaltung: | 13.09.2018 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 17.09.2018 |
Referierte Publikation: | Nein |