Моделирование процесса кристаллизациипри лазерной сварке со сквозным проплавлением пластин большой толщины
Simulation of solidification during keyhole laser welding of thick plates
- A method of solving the thermo-fluid dynamics problem is presented, enabling the prediction of the shape and dimensions of the weld pool during keyhole laser welding of thick plates. It is shown that the rear weld pool boundary can be satisfactorily approximated by a set of superellipses (Lamé curves). The presence of a convex rear weld pool boundary in the mid-plane has been observed experimentally and reproduced numerically. It was shown that in this zone the concentration of liquating impurities increases and the local solidification temperature decreases, contributing to the susceptibility to hot cracking.
Autor*innen: | Antoni ArtinovORCiD, Victor Karkhin, Marcel Bachmann, Michael Rethmeier |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Russisch |
Titel des übergeordneten Werkes (Russisch): | СВАРОЧНОЕ ПРОИЗВОДСТВО |
Jahr der Erstveröffentlichung: | 2024 |
Organisationseinheit der BAM: | 9 Komponentensicherheit |
9 Komponentensicherheit / 9.3 Schweißtechnische Fertigungsverfahren | |
Jahrgang/Band: | 5 |
Erste Seite: | 31 |
Letzte Seite: | 36 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Laser beam welding; Mathematical modeling; Superellipse; Thick steel plates; Three-dimensional crystallization |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Degradation von Werkstoffen | |
DOI: | 10.34641/SP.2023.1062.5.041 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 13.03.2024 |
Referierte Publikation: | Nein |