Failure Mechanisms Investigation by Means of in-situ Synchrotron Computed Tomography in Aluminum MMC-based Alloy Tailored for Additive Manufacturing
- Synchrotron X-ray computed tomography (SXCT) at BAMline has been paired with in-situ tensile loading to monitor damage evolution in LPBF Metal Matrix Composite (MMC) 7017 Aluminium alloy + 3 wt% Zr + 0.5 wt% TiC. The processing of the material leads formation to different categories of Zr-rich inclusions, precipitates and defects. In-situ SXCT test disclosed the critical role of the pre-cracks in the reinforcement phases in the failure mechanisms of LPBF MMC. The damage was initiated from lack-of-fusion defects and cracks propagated through coalescence with other defects.
Autor*innen: | Tatiana Mishurova |
---|---|
Dokumenttyp: | Posterpräsentation |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2023 |
Organisationseinheit der BAM: | 8 Zerstörungsfreie Prüfung |
8 Zerstörungsfreie Prüfung / 8.5 Röntgenbildgebung | |
DDC-Klassifikation: | Naturwissenschaften und Mathematik / Chemie / Analytische Chemie |
Freie Schlagwörter: | Additive manufacturing; BAMline; Synchrotron X-ray computed tomography; in-situ |
Themenfelder/Aktivitätsfelder der BAM: | Chemie und Prozesstechnik |
Material | |
Material / Additive Fertigung | |
Veranstaltung: | HZB Uer Meeting 2023 |
Veranstaltungsort: | Berlin, Germany |
Beginndatum der Veranstaltung: | 22.06.23 |
Enddatum der Veranstaltung: | 23.06.23 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 29.06.2023 |
Referierte Publikation: | Nein |