Investigating the microstructure and magnetic properties of La-Fe-Si microwires during fabrication and heat treatment process
- In this study, the optimized fabrication and evolution of the microstructure and magnetic Transition behavior of the melt-extraction LaFe11.2Si1.8 microwires have been studied. After the optimization of extraction technique (heating power 22 KW, feeding rate 30-50 mm/s, rotation velocity 1700 r/min), the content of La Fe,Si)13 phase in the as-extracted microwires was 54 wt% due to the high solidification velocity, which was increased to 85 wt% via annealing at 1373 K for 20 min. The amount of La(Fe,Si)13 phase was increased and the composition of La(Fe,Si)13 phase became more homogenized through peritectic reaction and short-distance diffusion in the microwires during annealing process. The coexistence of the nanocrystalline and amorphous structures contributed to the broad magnetic Transition temperature range of the as-extracted and annealed microwires. The annealed microwires exhibited a second-order magnetic transformation behavior and showed a maximum magnetic entropy ChangeIn this study, the optimized fabrication and evolution of the microstructure and magnetic Transition behavior of the melt-extraction LaFe11.2Si1.8 microwires have been studied. After the optimization of extraction technique (heating power 22 KW, feeding rate 30-50 mm/s, rotation velocity 1700 r/min), the content of La Fe,Si)13 phase in the as-extracted microwires was 54 wt% due to the high solidification velocity, which was increased to 85 wt% via annealing at 1373 K for 20 min. The amount of La(Fe,Si)13 phase was increased and the composition of La(Fe,Si)13 phase became more homogenized through peritectic reaction and short-distance diffusion in the microwires during annealing process. The coexistence of the nanocrystalline and amorphous structures contributed to the broad magnetic Transition temperature range of the as-extracted and annealed microwires. The annealed microwires exhibited a second-order magnetic transformation behavior and showed a maximum magnetic entropy Change jDSMjmax of 6.2 J/kgK and working temperature interval of 36.0 K under a magnetic field of 20 kOe.…
Autor*innen: | R. Zhang, M. Qian, Anja Waske, H. Shen, X. Zhang |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Journal of Alloys and Compounds |
Jahr der Erstveröffentlichung: | 2019 |
Organisationseinheit der BAM: | 8 Zerstörungsfreie Prüfung |
8 Zerstörungsfreie Prüfung / 8.0 Abteilungsleitung und andere | |
Verlag: | Elsevier B.V. |
Jahrgang/Band: | 794 |
Erste Seite: | 153 |
Letzte Seite: | 162 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | La(Fe,Si)13 phase; Magnetocaloric effect; Melt-extraction technique; Peritectic reaction; Short-distance diffusion |
Themenfelder/Aktivitätsfelder der BAM: | Material |
DOI: | 10.1016/j.jallcom.2019.04.196 |
ISSN: | 0925-8388 |
ISSN: | 1873-4669 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 29.05.2019 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 03.06.2019 |