Acoustic emission of fibre reinforced AlSi12CuMgNi alloy under compression

  • Typically, the near-eutectic Al-Si alloys consist of highly interconnected three-dimensional network of the eutectic Silicon (Si) and intermetallics embedded into Aluminium (Al) matrix. For further improvement of the mechanical properties of such alloys, often, one single ceramic reinforcement phase, e.g. silicon carbide (SiC) or aluminium oxide (Al2O3) in the form of fibres or particles is added. However, hybrid reinforcements (fibres and particles) can further improve wear resistance and fracture toughness, and additionally, reduce anisotropy of the material. The engineering of metal matrix composites (MMC) for specific application requirements benefits from a comprehensive knowledge of the failure behaviour. Therefore, damage evolution under compression was investigated on: - pure near-eutectic AlSi12CuMgNi matrix alloy - type I: matrix reinforced with random-planar oriented Al2O3 short fibres (15 vol.%) - type II: matrix reinforced with random-planar oriented Al2O3 short fibresTypically, the near-eutectic Al-Si alloys consist of highly interconnected three-dimensional network of the eutectic Silicon (Si) and intermetallics embedded into Aluminium (Al) matrix. For further improvement of the mechanical properties of such alloys, often, one single ceramic reinforcement phase, e.g. silicon carbide (SiC) or aluminium oxide (Al2O3) in the form of fibres or particles is added. However, hybrid reinforcements (fibres and particles) can further improve wear resistance and fracture toughness, and additionally, reduce anisotropy of the material. The engineering of metal matrix composites (MMC) for specific application requirements benefits from a comprehensive knowledge of the failure behaviour. Therefore, damage evolution under compression was investigated on: - pure near-eutectic AlSi12CuMgNi matrix alloy - type I: matrix reinforced with random-planar oriented Al2O3 short fibres (15 vol.%) - type II: matrix reinforced with random-planar oriented Al2O3 short fibres (7 vol.%) and additional SiC particles (15 vol.%) The analysis of damage mechanism was carried out in two rather independent but complementary studies. First, selected sister samples of every material were exposed to quasi-static compression (traverse control). The compression tests were interrupted at different strain levels. Miniature cylinders with a diameter of 1mm were extracted from the pre-strained samples and investigated by synchrotron computed tomography (SX-µCT) with a spatial resolution of about 0.7 µm. For the pure matrix alloy, microcracks are confined to the intermetallic particles and to the eutectic Si, hence no damage was observed in the Aluminium. The composite type II revealed a more effective strain accumulation (less damage) than type I at low plastic strain (up to 5 %), but a more catastrophic damage development due to cracking of the SiC clusters at higher strain levels. The second approach to study the damage initiation and accumulation in the materials subjected to compressive load was Acoustic Emission (AE) analysis. In this case the in-situ monitoring of the acoustic emission signal was performed during compression tests on specimens with dimension of several mm. For all three material types, AE activity set at 2% strain. Differences in AE behaviour of the three materials was proven based on AE hitrate, signal peak amplitudes as well as weighted peak frequencies (WPF). Future work focuses on combination of AE and SX-µCT aiming for more detailed knowledge on damage mechanism of metal matrix composites.zeige mehrzeige weniger

Volltext Dateien herunterladen

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Franziska BaenschORCiD
Koautor*innen:Sergei Evsevleev
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2021
Organisationseinheit der BAM:8 Zerstörungsfreie Prüfung
8 Zerstörungsfreie Prüfung / 8.1 Sensorik, mess- und prüftechnische Verfahren
8 Zerstörungsfreie Prüfung / 8.5 Röntgenbildgebung
Veröffentlichende Institution:Bundesanstalt für Materialforschung und -prüfung (BAM)
DDC-Klassifikation:Naturwissenschaften und Mathematik / Chemie / Analytische Chemie
Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Acoustic emission; Al-Si alloys; AlSi12CuMgNi; Tension
Themenfelder/Aktivitätsfelder der BAM:Chemie und Prozesstechnik
Material
Veranstaltung:Schall21
Veranstaltungsort:Online meeting
Beginndatum der Veranstaltung:24.02.2021
Enddatum der Veranstaltung:25.02.2021
URN:urn:nbn:de:kobv:b43-534268
URL:https://www.dgzfp.de/seminar/schall21
Verfügbarkeit des Dokuments:Datei für die Öffentlichkeit verfügbar ("Open Access")
Lizenz (Deutsch):License LogoCreative Commons - CC BY - Namensnennung 4.0 International
Datum der Freischaltung:30.09.2021
Referierte Publikation:Nein
Eingeladener Vortrag:Nein
Schriftenreihen ohne Nummerierung:BAM Präsentationen
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.