The bulging effect and its relevance in high power laser beam welding
- The present work deals with the recently confirmed widening of the weld pool interface, known as a bulging effect, and its relevance in high power laser beam welding. A combined experimental and numerical approach is utilized to study the influence of the bulge on the hot cracking formation and the transport of alloying elements in the molten pool. A technique using a quartz glass, a direct-diode laser illumination, a high-speed camera, and an infrared camera is applied to visualize the weld pool geometry in the longitudinal section. The study examines the relevance of the bulging effect on both, partial and complete penetration, as well as for different sheet thicknesses ranging from 8 mm to 25 mm. The numerical analysis shows that the formation of a bulge region is highly dependent on the penetration depth and occurs more frequently during partial penetration above 6 mm and complete penetration above 8 mm penetration depth, respectively. The location of the bulge correlates stronglyThe present work deals with the recently confirmed widening of the weld pool interface, known as a bulging effect, and its relevance in high power laser beam welding. A combined experimental and numerical approach is utilized to study the influence of the bulge on the hot cracking formation and the transport of alloying elements in the molten pool. A technique using a quartz glass, a direct-diode laser illumination, a high-speed camera, and an infrared camera is applied to visualize the weld pool geometry in the longitudinal section. The study examines the relevance of the bulging effect on both, partial and complete penetration, as well as for different sheet thicknesses ranging from 8 mm to 25 mm. The numerical analysis shows that the formation of a bulge region is highly dependent on the penetration depth and occurs more frequently during partial penetration above 6 mm and complete penetration above 8 mm penetration depth, respectively. The location of the bulge correlates strongly with the cracking location. The obtained experimental and numerical results reveal that the bulging effect increases the hot cracking susceptibility and limits the transfer of alloying elements from the top of the weld pool to the weld root.…
Autor*innen: | Antoni ArtinovORCiD, Xiangmeng MengORCiD, Nasim BakirORCiD, Ömer Üstündag, Marcel BachmannORCiD, Andrey GumenyukORCiD, Michael RethmeierORCiD |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | IOP Conference Series: Materials Science and Engineering |
Jahr der Erstveröffentlichung: | 2021 |
Organisationseinheit der BAM: | 9 Komponentensicherheit |
9 Komponentensicherheit / 9.3 Schweißtechnische Fertigungsverfahren | |
Veröffentlichende Institution: | Bundesanstalt für Materialforschung und -prüfung (BAM) |
Verlag: | IOP Publishing |
Jahrgang/Band: | 1135 |
Ausgabe/Heft: | 012003 |
Erste Seite: | 1 |
Letzte Seite: | 11 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Bulge effect; High-power laser beam welding; Metal mixing; Multi-physical modelling; Solidification cracking |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Veranstaltung: | 18th Nordic Laser Materials Processing Conference (18th NOLAMP) |
DOI: | 10.1088/1757-899X/1135/1/012003 |
URN: | urn:nbn:de:kobv:b43-539149 |
Verfügbarkeit des Dokuments: | Datei für die Öffentlichkeit verfügbar ("Open Access") |
Lizenz (Deutsch): | Creative Commons - CC BY - Namensnennung 4.0 International |
Datum der Freischaltung: | 06.12.2021 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 04.04.2022 |
Schriftenreihen ohne Nummerierung: | Wissenschaftliche Artikel der BAM |