Analysis of heterogeneous ageing of hnbr o rings
- Hydrogenated nitrile butadiene rubber (HNBR) elastomer was thermo-oxidatively aged at different temperatures up to 150°C. Fourier transform infrared spectroscopy (FTIR), compression stress relaxation (CSR) and IRHD microhardness were used to characterise the chemo-mechanical changes of HNBR O-rings during thermo-oxidative ageing. FTIR shows the development of carbonyl, methyl and ester groups but the nitrile content was not affected by ageing. The effect of sample geometry during CSR was investigated. CSR data were converted through integrated kinetic laws. The conversion has proven its sensibility to detect heterogeneous ageing. This was confirmed by the IRHD measurements across the section of O-rings. Oxidation profiles were determined by applying the model of Wise et al. to the IRHD experimental results.
Autor*innen: | Maha Zaghdoudi |
---|---|
Weitere Person: | Anja Kömmling, Matthias Jaunich, Dietmar Wolff |
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2023 |
Organisationseinheit der BAM: | 3 Gefahrgutumschließungen; Energiespeicher |
3 Gefahrgutumschließungen; Energiespeicher / 3.4 Sicherheit von Lagerbehältern | |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Angewandte Physik | |
Freie Schlagwörter: | CSR; FTIR; HNBR; Heterogeneous ageing; IRHD |
Themenfelder/Aktivitätsfelder der BAM: | Energie |
Energie / Kerntechnische Entsorgung | |
Material | |
Material / Degradation von Werkstoffen | |
Veranstaltung: | The 2023 Postgraduate Seminar - Advanced Structured Materials |
Veranstaltungsort: | Barcelona, Spain |
Beginndatum der Veranstaltung: | 20.02.2023 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 03.03.2023 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |