Dependence of the friction coefficient on roughness parameters during early stage fretting of (Al,Ti)N coated surfaces

  • Main focus was on the correlation of the coefficient of friction (COF) with the geometrical parameters of the surface during early stage of the running-in period. TiN, TiAlN and AlTiN coatings were prepared by using rotating cathode arc evaporation unit. The roughness of the WC-Co substrate Ra ranged from 0.05 to 0.2 µm and the coating thickness was 2.3 ± 0.2 µm. Part of the samples were subjected to the surface modification by the drag grinding finishing. Geometrical parameters of the surface were evaluated by means of atomic force microscopy (AFM) and fretting tests were conducted with 10 mm diameter alumina ball under 2 N load, 100 µm slip distance and the frequency of 10 Hz. It was found that the distribution of macroparticles strongly influences the geometrical parameters of the surface and the number of macroparticles increases with increasing Al content in the coating. In the case of the positive skewness Ssq of the coating surface, the kurtosis Sku provides a statisticallyMain focus was on the correlation of the coefficient of friction (COF) with the geometrical parameters of the surface during early stage of the running-in period. TiN, TiAlN and AlTiN coatings were prepared by using rotating cathode arc evaporation unit. The roughness of the WC-Co substrate Ra ranged from 0.05 to 0.2 µm and the coating thickness was 2.3 ± 0.2 µm. Part of the samples were subjected to the surface modification by the drag grinding finishing. Geometrical parameters of the surface were evaluated by means of atomic force microscopy (AFM) and fretting tests were conducted with 10 mm diameter alumina ball under 2 N load, 100 µm slip distance and the frequency of 10 Hz. It was found that the distribution of macroparticles strongly influences the geometrical parameters of the surface and the number of macroparticles increases with increasing Al content in the coating. In the case of the positive skewness Ssq of the coating surface, the kurtosis Sku provides a statistically significant effect on the COF, namely the COF depends inversely on the kurtosis Sku. The kurtosis value for TiN was the highest among as-deposited coatings, subsequently, the slowest increase rate in the COF was observed for the TiN coating.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Dependence of the friction coefficient.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:V. Podgursky, E. Adoberg, A. Surzenkov, E. Kimmari, M. Viljus, V. Mikli, Manfred Hartelt, Rolf WäscheORCiD, M. Síma, P. Kulu
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Wear
Jahr der Erstveröffentlichung:2011
Verlag:Elsevier
Verlagsort:Amsterdam
Jahrgang/Band:271
Ausgabe/Heft:5-6
Erste Seite:853
Letzte Seite:858
Freie Schlagwörter:AFM; COF; PVD coatings; Surface topography
DOI:10.1016/j.wear.2011.03.006
ISSN:0043-1648
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:21.10.2011
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.