Microstructure analysis and mechanical characterization of flame-retardant epoxy resins transferred to glass fiber composites via prepregs

  • The transfer of flame-retardant epoxy resin formulations to composites for structural and lightweight applications in the energy and transport sector can be complex and requires systematic investigation. Here, uncoated and silane-coated ammonium polyphosphate (APP, Si-APP) intumescent compounds are transferred to prepregs using a Bisphenol A diglycidyl ether (DGEBA) resin matrix to 0/90o bidirectional glass fibers with an aerial weight of 600 g/m2. Inorganic silicates (InSi) are added to improve the fire residues of the composites after combustion and the total amount of flame retardants in the resin formulations was 10% by weight. The prepregs' fiber volume content (FVC) is corroborated using in-process measurements and thermogravimetric analysis. This was found to be approximately 60% for the composites containing APP, which is ideal for load-bearing applications with high mechanical strength. However, the Si-APP containing prepregs showed an inconsistent FVC potentially due toThe transfer of flame-retardant epoxy resin formulations to composites for structural and lightweight applications in the energy and transport sector can be complex and requires systematic investigation. Here, uncoated and silane-coated ammonium polyphosphate (APP, Si-APP) intumescent compounds are transferred to prepregs using a Bisphenol A diglycidyl ether (DGEBA) resin matrix to 0/90o bidirectional glass fibers with an aerial weight of 600 g/m2. Inorganic silicates (InSi) are added to improve the fire residues of the composites after combustion and the total amount of flame retardants in the resin formulations was 10% by weight. The prepregs' fiber volume content (FVC) is corroborated using in-process measurements and thermogravimetric analysis. This was found to be approximately 60% for the composites containing APP, which is ideal for load-bearing applications with high mechanical strength. However, the Si-APP containing prepregs showed an inconsistent FVC potentially due to interactions with the commercial sizing of the glass fibers. The composites subsequently prepared are analysed for potential filtration effects of the additives via SEM after immobilization in a cured resin and platinum sputtering. The inter-laminar shear strength and the mechanical strength of the composites are compared via three-point bending tests. Additionally, the fire performance of the composites is analysed using cone calorimetry. It was found there was minimal impact of the loading of the flame retardants on the delamination of the composites and the flexural strength. However, the high density of the glass fibers possibly results in a suppression of the mode of action of the flame retardants in the composites. Therefore, the fire residues of the composites are further compared using SEM, and the flame-retardant modes of action upon transfer are investigated.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • EUROMAT_Poster_V3 .pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:S. Sunder
Koautor*innen:Maria Jauregui Rozo, Bernhard Schartel, H. Ruckdäschel
Dokumenttyp:Posterpräsentation
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2023
Organisationseinheit der BAM:7 Bauwerkssicherheit
7 Bauwerkssicherheit / 7.5 Technische Eigenschaften von Polymerwerkstoffen
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurbau
Freie Schlagwörter:Composites; Flame retardancy; Lightweight construction
Themenfelder/Aktivitätsfelder der BAM:Infrastruktur
Infrastruktur / Fire Science
Veranstaltung:FEMS EUROMAT 23
Veranstaltungsort:Frankfurt am Main, Germany
Beginndatum der Veranstaltung:03.09.2023
Enddatum der Veranstaltung:07.09.2023
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:13.12.2023
Referierte Publikation:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.