Bench-scale fire stability testing of carbon fibre reinforced polymer laminates with protective layers

  • Fire resistance testing of components made of carbon fibre reinforced polymers (CFRP) composites usually demands intermediate-scale or full-scale testing. In this study, a bench-scale test is presented as a practicable and efficient method to assess the improvement in structural integrity of CFRP with different protective interlayers during fire. Fire stability is one of the biggest issues of carbon fibre reinforced polymer (CFRP) composites, particularly when they are using in load bearing applications. As soon as the glass transition temperature of polymer matrix (100-200°C) is achieved, the composite loses its structural integrity, what leads to the distortion and failure. The principal fire stability test is based on simultaneous application of fire and mechanical load. Since the carbon fibres can transfer the tensile loads quite well, the compression load is chosen as a required mechanical load for a test. The fire tests were preceded by a static load test at room temperature toFire resistance testing of components made of carbon fibre reinforced polymers (CFRP) composites usually demands intermediate-scale or full-scale testing. In this study, a bench-scale test is presented as a practicable and efficient method to assess the improvement in structural integrity of CFRP with different protective interlayers during fire. Fire stability is one of the biggest issues of carbon fibre reinforced polymer (CFRP) composites, particularly when they are using in load bearing applications. As soon as the glass transition temperature of polymer matrix (100-200°C) is achieved, the composite loses its structural integrity, what leads to the distortion and failure. The principal fire stability test is based on simultaneous application of fire and mechanical load. Since the carbon fibres can transfer the tensile loads quite well, the compression load is chosen as a required mechanical load for a test. The fire tests were preceded by a static load test at room temperature to determine ultimate failure load. The specimen was loaded with a compression force until the failure load was reached, which was observed as a buckling. For the fire tests, 10% of compression failure load and direct flame of a fully developed fire (heat flux ≈ 180 kW m-2) were applied simultaneously to the specimen, while the time to failure was measured. The possibilities of bench-scale fire stability testing were presented by investigating new types of laminate structures, which exhibit promising flame retardancy and fireproof properties. The new approach of CFRP laminate differs with a protective concept. Every system consists of two different interlayers (titanium foil, thermoplastic foil PEI, ceramic layer WHIPOX, rubber tape Pyrostat, basalt fibres and kenaf fibres), where the one layer constitutes the fireproof protection, that delays the rise of temperature in the rest of laminate, and the second layer provides very good structural connection with carbon fibre layers, thus improves the mechanical integrity of CFRP composite in fire. The time to failure of CFRP composite was 17s. Protective systems significantly enhance the fire stability and increased time to failure by 3 to 10 times. Thicker specimens showed longer resistance time, however CFRP laminate with ceramic layer and titanium foil presented outstanding results and the best performance. The protection with Kenaf and basalt fibres offered a natural fibre solution with also good fire resistance performance Although bench-scale tests are limited with respect to assessing the performance of components and structures, they are valuable in the assessment of different materials concepts. Furthermore, the reduced effort of conducting bench-scale test (lower costs, time, personnel resources) makes it more practical and effective.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Tabaka_Session10.2_S11.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Weronika Tabaka
Koautor*innen:Bernhard Schartel
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2023
Organisationseinheit der BAM:7 Bauwerkssicherheit
7 Bauwerkssicherheit / 7.5 Technische Eigenschaften von Polymerwerkstoffen
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurbau
Freie Schlagwörter:Bench-scale testing; Carbon fibre reinforced polymer; Fire resistance
Themenfelder/Aktivitätsfelder der BAM:Infrastruktur
Infrastruktur / Fire Science
Veranstaltung:19th European meeting on Fire Retardant Polymeric Materials (FRPM23)
Veranstaltungsort:Dübendorf, Switzerland
Beginndatum der Veranstaltung:26.06.2023
Enddatum der Veranstaltung:29.06.2023
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:10.07.2023
Referierte Publikation:Nein
Eingeladener Vortrag:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.