Chloride‐induced steel corrosion in alkali‐activated fly ash mortar: Increased propensity for corrosion initiation at defects

  • Chloride contents at the steel–mortar interface that initiate steel corrosion were determined for carbon steel in alkali‐activated fly ash mortar for three different exposure conditions: exposure to 1 M NaCl solution; leaching in deionized water and then exposure to 1 M NaCl solution; and leaching in deionized water, aging in air at 20°C and natural CO2 concentration, and then exposure to 1 M NaCl solution. For comparison, a Portland cement mortar, exposed to 1 M NaCl solution, was studied. The median values of the corrosion‐initiating chloride contents (average over the full length of the rebar) in the alkali‐activated fly ash mortar varied between 0.35 and 1.05 wt% Cl with respect to binder, consistently lower than what was obtained for the Portland cement mortar, but with no clear trend regarding the exposure conditions. For most of the alkali‐activated fly ash mortar specimens, preferential corrosion at the connection between the working electrode and the external measurement setupChloride contents at the steel–mortar interface that initiate steel corrosion were determined for carbon steel in alkali‐activated fly ash mortar for three different exposure conditions: exposure to 1 M NaCl solution; leaching in deionized water and then exposure to 1 M NaCl solution; and leaching in deionized water, aging in air at 20°C and natural CO2 concentration, and then exposure to 1 M NaCl solution. For comparison, a Portland cement mortar, exposed to 1 M NaCl solution, was studied. The median values of the corrosion‐initiating chloride contents (average over the full length of the rebar) in the alkali‐activated fly ash mortar varied between 0.35 and 1.05 wt% Cl with respect to binder, consistently lower than what was obtained for the Portland cement mortar, but with no clear trend regarding the exposure conditions. For most of the alkali‐activated fly ash mortar specimens, preferential corrosion at the connection between the working electrode and the external measurement setup was observed, while preferential corrosion did not occur for the Portland cement mortar. Scanning electron microscopy and auxiliary experiments in synthetic solutions indicated that this behavior was caused by inhomogeneities at the steel–mortar interface in the alkali‐activated mortar, likely due to its peculiar rheological properties in the fresh state.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Gregor GluthORCiD, Gino EbellORCiD, Petr Hlavacek, Jürgen Mietz
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Materials and Corrosion
Jahr der Erstveröffentlichung:2020
Organisationseinheit der BAM:7 Bauwerkssicherheit
7 Bauwerkssicherheit / 7.4 Baustofftechnologie
7 Bauwerkssicherheit / 7.6 Korrosion und Korrosionsschutz
Veröffentlichende Institution:Bundesanstalt für Materialforschung und -prüfung (BAM)
Verlag:Wiley-VCH
Jahrgang/Band:71
Ausgabe/Heft:5
Erste Seite:749
Letzte Seite:758
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurbau
Freie Schlagwörter:Alkali-activated materials; Critical chloride content; Steel corrosion; Steel-concrete interface
Themenfelder/Aktivitätsfelder der BAM:Infrastruktur
Material
Material / Degradation von Werkstoffen
DOI:10.1002/maco.202011541
URN:urn:nbn:de:kobv:b43-507268
Verfügbarkeit des Dokuments:Datei für die Öffentlichkeit verfügbar ("Open Access")
Lizenz (Deutsch):License LogoCreative Commons - CC BY - Namensnennung 4.0 International
Datum der Freischaltung:06.05.2020
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:06.05.2020
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.