Analysis of industrial graphene-based flakes – first results on morphological characterization, sample preparation and chemical composition

  • Before industrial grade graphene could reach comparable quality to the controlled laboratory scale material, many challenges must be overcome. In order to bridge the gap between lab-scale and industrial-scale production is necessary to develop processes, equipment and measurement procedures to control the material features. One of the most crucial reasons of graphene’s limited commercialization is the lack of standard procedures to properly characterize and define the material chemical and structural properties down to the nanometer level. This leads to many issues regarding material synthesis repeatability, inappropriateness choice of measurands and measurement reproducibility which heavily affect the consistency of the material performance. For example, among all the different industrially produced real-world graphene, it is crucial to determine how many layers of graphene build the material. Products that are built by more than 10 layers should be more correctly referred asBefore industrial grade graphene could reach comparable quality to the controlled laboratory scale material, many challenges must be overcome. In order to bridge the gap between lab-scale and industrial-scale production is necessary to develop processes, equipment and measurement procedures to control the material features. One of the most crucial reasons of graphene’s limited commercialization is the lack of standard procedures to properly characterize and define the material chemical and structural properties down to the nanometer level. This leads to many issues regarding material synthesis repeatability, inappropriateness choice of measurands and measurement reproducibility which heavily affect the consistency of the material performance. For example, among all the different industrially produced real-world graphene, it is crucial to determine how many layers of graphene build the material. Products that are built by more than 10 layers should be more correctly referred as nanosized graphite, a problem that is often regarded as the “fake graphene” issue. In our study, a comparative analysis is performed on two different series (G5 and G6) of industrial graphene powders, each series produced with four types of functionalization: raw graphene, oxygen-functionalized, nitrogen-functionalized and fluorine-functionalized. All the 8 sample variants were analyzed from a chemical and morphological point of view in the form of powders prepared as slightly pressed in metallic sample holders. The results of the comparative chemical analyses XPS and EDS show a good agreement in the concentration values for all the elements present in the samples, despite the different analysis volumes addressed by the two techniques. For this reason, the samples can be considered homogeneous in both lateral and vertical direction. A clear influence of the morphology on the composition is evident. Therefore, such correlative measurements of morphology and composition are necessary for a comprehensive characterization of industrial graphene flakes. Protocols for reliable characterization of industrial graphene flakes are in progress.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • MM2022_presentation_ChemelloEtAl.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Giovanni Chemello
Koautor*innen:Jörg Radnik, Vasile-Dan Hodoroaba
Dokumenttyp:Vortrag
Veröffentlichungsform:Präsentation
Sprache:Englisch
Jahr der Erstveröffentlichung:2022
Organisationseinheit der BAM:6 Materialchemie
6 Materialchemie / 6.1 Oberflächen- und Dünnschichtanalyse
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:EDS; Functionalized graphene; Graphene powder; SEM; XPS
Themenfelder/Aktivitätsfelder der BAM:Material
Material / Nano
Veranstaltung:Microscopy and Microanalysis 2022
Veranstaltungsort:Portland, OR, USA
Beginndatum der Veranstaltung:31.07.2022
Enddatum der Veranstaltung:04.08.2022
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:11.08.2022
Referierte Publikation:Nein
Eingeladener Vortrag:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.