Fatigue Behavior at Elevated Temperature of Alloy EN AW-2618A
- The influence of test temperature and frequency on the fatigue life of the alloy EN AW-2618A (2618A) was characterized. The overaged condition (T61 followed by 1000 h/230 °C) was investigated in load-controlled tests with a stress ratio of R = -1 and two test frequencies (0.2 Hz, 20 Hz) at room temperature and at 230°C, respectively. An increase in the test temperature reduces fatigue life, whereby this effect is more pronounced at lower stress amplitudes. Decreasing the test frequency in tests at high temperatures further reduces the service life.
Autor*innen: | Birgit Skrotzki |
---|---|
Weitere Person: | Ying Han, Julius Kruse, Jan Radners, Mauro Madia, Philipp von Hartrott |
Dokumenttyp: | Vortrag |
Veröffentlichungsform: | Präsentation |
Sprache: | Englisch |
Jahr der Erstveröffentlichung: | 2024 |
Organisationseinheit der BAM: | 5 Werkstofftechnik |
5 Werkstofftechnik / 5.2 Metallische Hochtemperaturwerkstoffe | |
9 Komponentensicherheit | |
9 Komponentensicherheit / 9.4 Integrität von Schweißverbindungen | |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | Aluminium alloy; Damage behavior; EN AW 2618A; Fatigue; Overaging |
Themenfelder/Aktivitätsfelder der BAM: | Material |
Material / Degradation von Werkstoffen | |
Veranstaltung: | ICAA19 International Conference on Aluminum Alloys |
Veranstaltungsort: | Atlanta, GA, USA |
Beginndatum der Veranstaltung: | 23.06.2024 |
Enddatum der Veranstaltung: | 28.06.2024 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 01.07.2024 |
Referierte Publikation: | Nein |
Eingeladener Vortrag: | Nein |