Tetragonality mapping of martensite in high-carbon steel by EBSD
- The locally varying tetragonality in martensite grains of a high-carbon steel (1.2 mass percent C) was resolved by electron backscatter diffraction (EBSD) with a spatial resolution in the order of 100 nm. Compared to spatially integrating X-ray diffraction, which yielded an average tetragonality fo c/a=1.05, the EBSD measurements in the scanning electron microscope allowed to image a local variation of the lattice papameter ration c/a in the range of 1.02 ≤ c/a ≤ 1.07. The local variation of tetragonality is confirmed by two different EBSD data analysis approaches based on the fitting of simulated to experimental EBSD patterns. The resulting EBSD-based tetragonality maps are pointing to a complex interaction of carbon concentration and local lattice distortions during the formation process of martensitic structures.
Autor*innen: | Gert Nolze, A. Winkelmann, G. Cios, T. Tokarski |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Materials Characterization |
Jahr der Erstveröffentlichung: | 2021 |
Organisationseinheit der BAM: | 5 Werkstofftechnik |
5 Werkstofftechnik / 5.1 Mikrostruktur Design und Degradation | |
Verlag: | Elsevier Inc. |
Jahrgang/Band: | 175 |
Erste Seite: | 111040 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | EBSD; Martensite; Pattern matching; Tetragonal distortion |
Themenfelder/Aktivitätsfelder der BAM: | Material |
DOI: | 10.1016/j.matchar.2021.111040 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 29.03.2021 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 31.05.2021 |