Near zero shrinkage porous Al2O3 prepared via 3D-printing and reaction bonding

  • Porous Al2O3 with high porosity (~45%), remarkable flexural strength (~70 MPa), and low dimensional change (~1–2%), was produced by indirect 3D printing and reaction bonding. Coarse Al with good flowability was carried out printing green body. The green body was heat treated to get fully oxidized, volume expansion during oxidation simultaneously formed strong neck bonding, not only brought good strength, but also restricted shrinkage. Porous Al2O3 with architecture of macro pores designed by 3D printing and micro pores in the strut formed by packing of particles was obtained. The near zero shrinkage can facilitate precise design of product with complex shape.

Volltext Dateien herunterladen

  • 1-s2.0-S0167577X15002232-main.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Dongxu Yao, Cynthia Wirth, Y.-P. Zeng, D. Jiang, Jens GünsterORCiD, J. Heinrich
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Materials letters
Jahr der Erstveröffentlichung:2015
Verlag:North-Holland Publ. Co.
Verlagsort:Amsterdam
Jahrgang/Band:147
Erste Seite:116
Letzte Seite:118
Freie Schlagwörter:Al2O3 reaction bonding
DOI:10.1016/j.matlet.2015.02.037
ISSN:0167-577x
ISSN:1873-4979
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:25.11.2015
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.