Microstructural investigation using advanced TEM techniques of inner ocide layers formed on T92 steel in oxyfuel environment
- T92 steel was oxidized at 650 °C for 1000 h in dry and wet oxyfuel gases. The microstructure of inner oxide layer was investigated using scanning transmission electron microscopy and energy dispersive spectroscopy on thin lamellas of oxide cross-sections. The oxides were composed of fine equiaxed grains and separated into Fe-rich and Cr-rich regions. Fe-rich regions were wustite and iron sulphide while Cr-rich regions consisted of Fe-Cr spinel with different stoichiometries. Precipitates of (W,Mo)-rich oxides were formed within the oxide scale and beneath the oxide/alloy interface. Often iron sulphide and (W,Mo)-rich oxide were surrounded by Cr-rich spinel.
Autor*innen: | K. Chandra, Ilona Dörfel, N. Wollschläger, Axel KranzmannORCiD |
---|---|
Dokumenttyp: | Zeitschriftenartikel |
Veröffentlichungsform: | Verlagsliteratur |
Sprache: | Englisch |
Titel des übergeordneten Werkes (Englisch): | Corrosion Science |
Jahr der Erstveröffentlichung: | 2019 |
Organisationseinheit der BAM: | 5 Werkstofftechnik |
5 Werkstofftechnik / 5.1 Mikrostruktur Design und Degradation | |
Verlag: | Elsevier |
Jahrgang/Band: | 148 |
Erste Seite: | 94 |
Letzte Seite: | 109 |
DDC-Klassifikation: | Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten |
Freie Schlagwörter: | High temperature corrosion; Internal oxidation; Oxidation; STEM; Steel |
Themenfelder/Aktivitätsfelder der BAM: | Material |
DOI: | 10.1016/j.corsci.2018.12.008 |
ISSN: | 0010-938X |
ISSN: | 1879-0496 |
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
Datum der Freischaltung: | 22.02.2019 |
Referierte Publikation: | Ja |
Datum der Eintragung als referierte Publikation: | 22.02.2019 |