In situ shrinkage measurement during pressure-assisted sintering of low temperature co-fired ceramic panels

  • Shrinkage measurements of miniaturized low temperature co-fired ceramics (LTCC) samples under load typically lead to collapsing of the samples, which hampers the characterization of shrinkage up to full densification. In this paper, a measurement setup is presented, which allows for in situ shrinkage measurements of practical, large LTCC panels during pressure-assisted sintering in a sintering press. The shrinkage behavior of two commercial LTCC systems (GreenTape 951 and Ceramtape GC) has been measured under loads of up to 1 MPa. No crushing of the specimens was observed and reproducible characterization of shrinkage up to full densification has been performed. Based on comparisons to thermomechanical analyzer measurements in this and other studies, it was found that the in situ approach is much better suited for shrinkage characterization of LTCC under load. Reproducibility and accuracy of the method are discussed and practical as well as more academic applications are proposed.

Volltext Dateien herunterladen

  • Mieller_et_al-2017-International_Journal_of_Applied_Ceramic_Technology.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar
Metadaten
Autoren/innen:Björn Mieller, Torsten Rabe, V. Rangelov
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):International Journal of Applied Ceramic Technology
Jahr der Erstveröffentlichung:2017
Organisationseinheit der BAM:5 Werkstofftechnik
5 Werkstofftechnik / 5.5 Technische Keramik
Jahrgang/Band:14
Ausgabe/Heft:2
Erste Seite:245
Letzte Seite:251
DDC-Klassifikation:Technik, Medizin, angewandte Wissenschaften / Ingenieurwissenschaften / Ingenieurwissenschaften und zugeordnete Tätigkeiten
Freie Schlagwörter:Low temperature; Shrinkage; Sinter/sintering
Themenfelder/Aktivitätsfelder der BAM:Material
DOI:https://doi.org/10.1111/ijac.12634
URL:http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcAuth=Alerting&SrcApp=Alerting&DestApp=WOS&DestLinkType=FullRecord;UT=WOS:000397509500016
ISSN:1546-542X
ISSN:1744-7402
Verfügbarkeit des Volltexts:Volltext-PDF im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:13.03.2017
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:18.04.2017